DIAMETER: 0.345″+.000″/-.005″
THICKNESS: 0.020″+/-.003″
PARALLELISM: 5 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: NONE, NOT REQUIRED.
SCD1174-02B
$50.00
SAPPHIRE WINDOW UNCOATED
0.345″DIA. X 0.020″THK.
15 in stock
SKU: SCD1174-02B
Category: SAPPHIRE WINDOW
Weight | 0.1 lbs |
---|
Related products
SCD1871-WIT2
CONFIGURATION: DISC, PLANE-PARALLELDIAMETER: 1.000"+.000"/-.005"
THICKNESS: 2.50mm +/- 0.05mm
PARALLELISM: 0.03 DEGREES MAXIMUM.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
CLEAR APERTURE: CENTRAL 0.800" MINIMUM DIAMETER,
2 FACES.
SURFACE ACCURACY: PWR: 5 WAVES MAXIMUM, 2 FACES
IRRG: 2 WAVES MAXIMUM, 2 FACES
SURFACE QUALITY: 60-40 PER MIL-C-48497, 2 FACES.
SURFACE ROUGHNESS: 20 ANGSTROMS Ra MAXIMUM.
MATERIAL TYPE/QUALITY: SAPPHIRE, SCHLIEREN GRADE,
NO TWINNING, C-AXIS PERP.
TO FACES (NO BIREFRINGENCE)
COATING: NONE, UNCOATED SUBSTRATE.
AK0910750040
DIAMETER TOLERANCE: +/-.002"THICKNESS TOLERANCE: +/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 1 POLISHED FACE.
SURFACE FINISH: 80-50 PER MIL-O-13830, 1 FACE.
16 MICROINCH NOMINAL, 1 FACE.
MATERIAL QUALITY: OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
SCD0651-01C
DIAMETER: 0.500"+.000"/-.001"THICKNESS: 0.0235"+/-.0005"
PARALELLISM: CONTROLLED BY THICKNESS TOLERANCE.
FLATNESS: 1 WAVE MAXIMUM, 2 FACES.
FINISH: 10 MICROINCH NOMINAL, 2 FACES.
OD EDGE: 0.012" FULL RADIUS
OD EDGE FINISH: BRUSH POLISH.
MATERIAL QUALITY: NON-OPTICAL
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
MSW112/125A
DIAMETER: 1.125"+/-.004"THICKNESS: 0.125"+/-.003"
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
EDGE BEVEL: 0.010"/0.015" X 45deg, 2 PLACES.
SURFACE QUALITY: 80-50 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
A00E10500157
DIAMETER TOLERANCE: +/-.002"THICKNESS TOLERANCE: +/-.004"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 OR BETTER, 2 FACES.
MATERIAL QUALITY: UNKNOWN.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
SCD1523-01A
DIAMETER: 0.500"+/-.002"THICKNESS: 0.125"+/-.002"
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES
EDGE BEVEL: 0.010"/0.015" X 45deg, 2 PLACES.
SURFACE FINISH: 80-50 PER MIL-O-13830, 2 FACES.
MATERIAL QUALITY: OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: ANTIREFLECTIVE COATED FOR MAXIMUM
TRANSMISSION AT 880 NANOMETERS WITH A
NORMAL INCIDENCE ANGLE, APPLIED TO 1 FACE
ONLY.
MARKING: ARROW ON OD SURFACE POINTING TOWARDS
COATED FACE.
SCD1708-01A
DIAMETER: 0.116"+/-.001"THICKNESS: 0.038"+/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: BROADBAND ANTIREFLECTIVE WITH MgF2 FOR
MAXIMUM TRANSMISSION IN THE VISIBLE
ONE FACE ONLY.
SCD2378-02B
CONFIGURATION: DISC (W/ OD FLATS), PLANE-PARALLELDIAMETER: 100.00mm +/- 0.10mm
THICKNESS: 0.025"+/-.0005"
PARALLELISM: 0.000138" T.T.V. ( 0.0035mm )
PRIMARY FLAT SIZE: 32.00mm +/- 2.00mm WIDTH
PRIMARY FLAT LOCATION: RANDOM.
SECONDARY FLAT SIZE: 18.00mm +/- 2.00mm WIDTH.
SECONDARY FLAT LOCATION: 90 deg FROM PRIMARY FLAT.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
SURFACE QUALITY: 80-50 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION:(0001)