DIAMETER: 25.40mm + 0.00mm /- 0.13mm
THICKNESS: 3.15mm +/- 0.13mm
PARALLELISM: 2 ARC SECONDS MAXIMUM.
FLATNESS: 1/10 WAVE MAXIMUM WITHIN THE CENTRAL 80%
OF THE DIAMETER, 2 FACES.
SURFACE FINISH: 80-50 PER MIL-O-13830 WITHIN THE
CENTRAL 80% OF THE DIAMETER, 2 FACES.
EDGE BEVEL: 0.50mm +/- 0.25mm X 45deg, 2 PLACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, PREMIUM GRADE,
FREE OF TWINS, SMALL ANGLE GRAIN
BOUNDARIES, STRIAE, AND SCATTERING
CENTERS.
CRYSTALLOGRAPHIC ORIENTATION: C-AXIS PARALLEL AND
IN THE PLANE OF FACES, 90 DEG +/- 10deg.
SCD1324-01A
$260.00
SAPPHIRE WINDOW
25.40mmDIA. X 3.15mmTHK.
14 in stock
SKU: SCD1324-01A
Category: SAPPHIRE WINDOW
Weight | 0.1 lbs |
---|
Related products
AL0EW0393197
DIAMETER: 0.393"+/-.0020"THICKNESS: 0.197"+/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 5 WAVES MAXIMUM @ 0.633um, 2 FACES.
SURFACE FINISH: 20-10 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE
CRYSTALLOGRAPHIC ORIENTATION: (0001)
MSW25M/020M
DIAMETER: 25.00mm +/- 0.05mmTHICKNESS: 2.00mm +/- 0.05mm
PARALLELISM: 5 ARC MINUTES MAXIMUM.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 60-40 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
A00E10500157
DIAMETER TOLERANCE: +/-.002"THICKNESS TOLERANCE: +/-.004"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 OR BETTER, 2 FACES.
MATERIAL QUALITY: UNKNOWN.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
SCD1365-01B
DIAMETER: 20.00mm + 0.00mm /- 0.10mmTHICKNESS: 2.00mm +/- 0.10mm
PARALLELISM: 3 ARC MINUTES MAXIMUM.
EDGE BEVEL: SLIGHT PROTECTIVE BEVEL, 2 PLACES.
SURFACE FIGURE: 2.0 WAVES/INCH MAXIMUM, 2 FACES.
TRANSMITTED WAVEFRONT ERROR: 1/2 WAVE MAXIMUM.
SURFACE QUALITY: 60-40 SCRATCH/DIG PER
MIL-O-13830, TWO FACES
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: DUAL BAND ANTIREFLECTIVE COATED FOR
> 99.0% TRANSMISSION AT 2.94 MICRONS AND
85.0% MINIMUM TRANSMISSION AT 670nm, WITH
A 0-12deg INCIDENCE ANGLE, APPLIED TO
BOTH FACES. (RANDOM POLARIZATION)
DAMAGE THRESHOLD: 130 J/cm2, 10 Hz, 100usec PULSE
SCD1708-01A
DIAMETER: 0.116"+/-.001"THICKNESS: 0.038"+/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: BROADBAND ANTIREFLECTIVE WITH MgF2 FOR
MAXIMUM TRANSMISSION IN THE VISIBLE
ONE FACE ONLY.
SCD2378-02B
CONFIGURATION: DISC (W/ OD FLATS), PLANE-PARALLELDIAMETER: 100.00mm +/- 0.10mm
THICKNESS: 0.025"+/-.0005"
PARALLELISM: 0.000138" T.T.V. ( 0.0035mm )
PRIMARY FLAT SIZE: 32.00mm +/- 2.00mm WIDTH
PRIMARY FLAT LOCATION: RANDOM.
SECONDARY FLAT SIZE: 18.00mm +/- 2.00mm WIDTH.
SECONDARY FLAT LOCATION: 90 deg FROM PRIMARY FLAT.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
SURFACE QUALITY: 80-50 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION:(0001)
SCD2191-02A
CONFIGURATION: DISC (W/ OD FLAT), PLANE-PARALLELDIAMETER: 2.000"+/-.002"
THICKNESS: 0.0157"+/-.0010"
OD FLAT SIZE: 0.625"+/-.050" WIDTH
OD FLAT LOCATION: RANDOM
PARALLELISM: 0.001" MAXIMUM T.I.R.
BOW: 0.0008" MAXIMUM T.I.R.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
SURFACE FINISH: 80-50 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
COATING: NONE, NOT REQUIRED.
SCD1435-01A
MAJOR DIAMETER: 0.348"+/-.002"MINOR DIAMETER: 0.248"+.000"/-.005"
OVERALL THICKNESS: 0.097" REF.
MAJOR DIAMETER THICKNESS: 0.062"+/-.002"
MINOR DIAMETER HEIGHT: 0.035"+/-.005"
CONCENTRICITY OF DIAMETERS: NOT SPECIFIED.
PARALLELISM: 3 ARC MINUTES MAXIMUM
EDGE BEVEL: 0.005" NOMINAL X 45deg, 3 PLACES.
FLATNESS: 1 WAVE/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 60-40 PER MIL-O-13830, 2 FACES.
CLEAR APERTURE: CENTRAL 90% MINIMUM DIAMETER FACE
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL WHITE
GRADE (CSI).
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: NONE, NOT REQUIRED.