MAJOR DIAMETER: 0.748″+/-.002″
OD TAPER ANGLE: 10deg +/- 15min. (320 MESH FINISH)
ROUNDNESS: NOT TO EXCEED 0.002″ T.I.R.
CONCENTRICITY: MAJOR AND MINOR DIAMETERS WITHIN
0.002″ T.I.R.
THICKNESS TOLERANCE: +/-.002″
PARALLELISM: 0.001″/INCH MAXIMUM, T.I.R.
FLATNESS: 0.0002″/INCH MAXIMUM T.I.R, 2 FACES.
EDGE BEVELS: MAJOR DIA. EDGE: 0.025″+/-.005″
X 45deg, 1 PLACE. (320 MESH FINISH)
MINOR DIA. EDGE: 0.015″+/-.005″
X 45deg, 1 PLACE. (320 MESH FINISH)
SURFACE FINISH: 50-20 PER MIL-O-13830, 2 FACES.
MATERIAL QUALITY: CSI WHITE, ULTRA-VIOLET GRADE.
CRYSTALLOGRAPHIC ORIENTATION: (0001)
SCD1442-01B
$495.00
SAPPHIRE WINDOW 0.748″DIA.
0.748″MAJOR DIA. X 0.080″THK.
1 in stock
SKU: SCD1442-01B
Category: SAPPHIRE WINDOW
Weight | 0.1 lbs |
---|
Related products
SCD1708-01A
DIAMETER: 0.116"+/-.001"THICKNESS: 0.038"+/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: BROADBAND ANTIREFLECTIVE WITH MgF2 FOR
MAXIMUM TRANSMISSION IN THE VISIBLE
ONE FACE ONLY.
MSW25M/020M
DIAMETER: 25.00mm +/- 0.05mmTHICKNESS: 2.00mm +/- 0.05mm
PARALLELISM: 5 ARC MINUTES MAXIMUM.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 60-40 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
AL0EW0393197
DIAMETER: 0.393"+/-.0020"THICKNESS: 0.197"+/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 5 WAVES MAXIMUM @ 0.633um, 2 FACES.
SURFACE FINISH: 20-10 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE
CRYSTALLOGRAPHIC ORIENTATION: (0001)
MSW10M/010M
DIAMETER: 10.00mm +/- 0.05mmTHICKNESS: 1.00mm +/- 0.05mm
PARALLELISM: 5 ARC MINUTES MAXIMUM.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 60-40 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
A00E10500157
DIAMETER TOLERANCE: +/-.002"THICKNESS TOLERANCE: +/-.004"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 OR BETTER, 2 FACES.
MATERIAL QUALITY: UNKNOWN.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
A10910787019
DIAMETER: 20.00mm +/- 0.05mmTHICKNESS: 0.50mm +/- 0.05mm
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 OR BETTER, 1 FACE.
FINE GROUND OTHER FACE.
MATERIAL QUALITY: OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: C-AXIS PERPENDICULAR
TO FACES, (0001) NOMINAL.
SCD3630-05B
CONFIGURATION: DISC, W/ OD FLAT, PLANE-PARALLELDIAMETER: 3.750"+.000"/-.005"
THICKNESS: 0.041"+/-.001"
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
PARALLELISM: 2 ARC SECONDS MAXIMUM
TRANSMITTED WAVEFRONT ERROR: < 1.0 WAVE @ 633nm.
RMS SLOPE ERROR: < 0.25 WAVE/cm @ 633nm.
SURFACE QUALITY: 20-10 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, LASER GRADE.
CRYSTALLOGRAPHIC ORIENTATION: a-PLANE +/- 15 ARC
MINUTES, WITH THE
c-AXIS 45 DEGREES TO
THE OD FLAT.
COATING: NONE, NOT REQUIRED.
SCD1481-01A
DIAMETER: 12.50mm + 0.00mm /- 0.10mmTHICKNESS: 3.00mm +/- 0.10mm
PARALLELISM: NOT SPECIFIED
EDGE BEVEL: PROTECTIVE EDGE BREAK, 2 PLACES.
TRANSMITTED WAVEFRONT ERROR: 1/10 WAVE MAXIMUM.
SURFACE FINISH: 40-20 PER MIL-O-13830, 2 FACES.
MATERIAL QUALITY: OPTICAL GRADE
CRYSTALLOGRAPHIC ORIENTATION: C AXIS PERPENDICULAR
TO THE FACES WITHIN 2 DEGREES.