DIAMETER: 1.000″+.000″/-.010″
CENTER THICKNESS: 0.350″+/-.020″
WEDGE ANGLE: 20.0 DEGREES +/- 0.10 DEGREE
EDGE BEVEL: PROTECTIVE EDGE BREAK, 2 PLACES.
SURFACE ACCURACY: 1/4 WAVE MAXIMUM, 2 FACES.
SURFACE QUALITY: 60-40 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: (0001)
COATING: ANTIREFLECTIVE COATING FOR MAXIMUM
TRANSMISSION FROM 1.0 TO 2.5 MICRONS
WITH A NORMAL INCIDENCE ANGLE, APPLIED
TO BOTH FACES.
SCD1952-01A
$330.00
SAPPHIRE WEDGED WINDOW COATED
1.000″DIA. X 0.350″CENTER THK
1 in stock
SKU: SCD1952-01A
Category: SAPPHIRE WEDGED
Weight | 0.1 lbs |
---|
Related products
SCD4208-02A
Diameter: 2.000"+.000"/-.004" Thickness: 0.197"+/-.004" (High Side of Wedge) Edge Bevel: Light Protective Bevel, Both Edges Wedge Angle: 2.0 Degrees +/- 10 Arc Minutes Surface Accuracy: Not Specified. Surface Quality: 60-40 Per MIL-PRF-13830, Both Faces Material Type / Quality: Sapphire, Optical Grade Crystallographic Orientation: c-Plane Coating: None, Uncoated SubstrateSCD4324-02A
Diameter: 2.000"+/-.003" Thickness: 0.195"+/-.004" (High Side of Wedge) Edge bevels: 0.025" Maximum Face Width, Both Egdes Wedge: 4.0 Degrees +/- 30 Arc Minutes Suirface Figure: Power: 1 Wave Maximum @ 633nm, Both Faces Irregularity: 1/2 Wave Maximum @ 633nm, Both Faces Surface Quality: 40-20 Per Mil-PRF-13830, Both Faces Surface Roughness: < 50 Angstroms RMS, Both Faces Clear Aperture: Central 1.700" Diameter, Both Faces Material Type / Quality: Sapphire, Optical Grade Crystallographic Orientation: c-Plane Marking: Fiduciary Marks on OD Surface Designationg the Low and theHigh Side of the Wedge Coating: None, Not RequiredSCD3015-02A
DIAMETER: 0.625"+/-.002"THICKNESS: 0.072"+/-.002" (LOW SIDE)
WEDGE ANGLE: 3.0 DEGREES +/- 0.25 DEGREE
EDGE BEVELS: LIGHT PROTECTIVE BEVEL, 2 PLACES.
SURFACE ACCURACY: NOT SPECIFIED.
SURFACE FINISH: 80-50 PER MIL-PRF-13830, 2 FACES.
CLEAR APERTURE: CENTRAL 85% OF DIAMETER FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: NONE, NOT REQUIRED.
SCD2777-02D
DIAMETER: 100.00mm +/- 0.10mmTHICKNESS: 2.00mm +/- 0.10mm HIGH SIDE AT OD FLAT
WEDGE ANGLE: 1.30 mrad +/- 0.30 mrad (4.5 MINUTE)
FLATNESS: 1 WAVE/INCH MAXIMUM @ 633um, 2 FACES.
OD FLAT SIZE: 32.50mm +/- 2.50mm WIDE, ONE PLACE
OD FLAT LOCATION: PERPENDICULAR TO A-AXIS.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
SURFACE FINISH: 20-10 PER MIL-PRF-13830, 2 FACES.
SURFACE ROUGHNESS: 25 ANGSTROMS MAXIMUM, 2 FACES.
EDGE CHIPS: 0.50mm MAXIMUM.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE
CRYSTALLOGRAPHIC ORIENTATION: (0001).
COATING: NONE, NOT REQUIRED
SCD1930-02A
DIAMETER: 10.00mm +/- 0.025mmTHICKNESS: 1.52mm +/- 0.05mm
WEDGE ANGLE: 3.0 to 5.0 ARC MINUTES.
EDGE BEVEL: 0.10mm/0.20mm X 45deg, 2 PLACES.
SURFACE ACCURACY: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 60-40 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: (0001)
COATING: NONE, NOT REQUIRED.
A61E10590080
DIAMETER: 0.590"+/-.0020"THICKNESS: 0.080"+/-.0020"
WEDGE ANGLE: 0.5 TO1.0 DEG
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 PER MIL-O-13830, 2 FACES.
MATERIAL QUALITY: OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: C-AXIS (0001)
SCD4373-02A
Diameter: 25.40mm +.000/- 0.10mm Thickness: 20.50mm +/- 0.10mm (High Side of Wedge) 10.00mm Reference Only (Low Side of Wedge) Wedge Angle: 22.50 Degrees +/- 1.0 Degree Edge Bevels: 0.20mm / 0.30mm x 45 Degrees, Both Edges Surface Accuracy: Power: 5 Fringes Maximum @ 633nm, Both Faces Irregularity: 3 Fringes Maximum @ 633nm, Both Faces Surface Quality: 60-40 per MIL-PRF-13830, Both Faces Material Type / Quality: Sapphire, Optical Grade Marking: "Al203" per Drawing T0026368 Coating: None, Not RequiredSCD1923-02A
DIAMETER: 9.00mm + 0.00mm /- 0.10mmTHICKNESS: 0.50mm +/- 0.05 (AT LOW SIDE OF WEDGE)
WEDGE ANGLE: 0.50 DEGREES +/- 0.10 DEGREES
FLATNESS: NOT SPECIFIED
SURFACE FINISH: 60-40 PER MIL-O-13830, 2 FACES.
MATERIAL QUALITY: OPTICAL GRADE (AS-SUPPLIED).
CRYSTALLOGRAPHIC ORIENTATION: C-AXIS PERPENDICULAR
TO FACES, (0001) NOMINAL
MARKING: MARK ARROW ON THE OD SURFACE POINTING
TOWARDS THE LOW SIDE OF THE WEDGE.
COATING: NONE, UNCOATED SUBSTRATE.