CONFIGURATION: DISC/TRUNCATED, PLANE-PARALLEL
DIAMETER: 63.00mm +/- 0.25mm
TRUNCATED WIDTH: 58.00mm +/- 0.25mm
THICKNESS: 3.00mm +/- 0.20mm
EDGE BEVEL: LIGHT PROTECTIVE BEVELS, ALL EDGES.
TRANSMITTED WAVEFRONT ERROR: 1/10 WAVE RMS MAXIMUM
AT 1.064um.
SURFACE QUALITY: 40-20 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: (0001) NOMINAL
COATING: ANTIREFLECTIVE COATED FOR < 0.25%
REFLECTANCE PER SURFACE AT 1.064um
WITH A NORMAL INCIDENCE ANGLE, APPLIED
TO BOTH FACES.
ADHESION: PER MIL-C-675A
DURABILITY: PER MIL-C-675A
TEMPERATURE STABILITY:PER MIL-M-14806A
SCD2044-01A
$1,450.00
SAPPHIRE WINDOW TRUNCATED CTD
63.00mm DIA. X 3.00mm THK.
2 in stock
SKU: SCD2044-01A
Category: SAPPHIRE WINDOW
Weight | 0.1 lbs |
---|
Related products
A00E10500157
DIAMETER TOLERANCE: +/-.002"THICKNESS TOLERANCE: +/-.004"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 OR BETTER, 2 FACES.
MATERIAL QUALITY: UNKNOWN.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
SCD3630-05B
CONFIGURATION: DISC, W/ OD FLAT, PLANE-PARALLELDIAMETER: 3.750"+.000"/-.005"
THICKNESS: 0.041"+/-.001"
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
PARALLELISM: 2 ARC SECONDS MAXIMUM
TRANSMITTED WAVEFRONT ERROR: < 1.0 WAVE @ 633nm.
RMS SLOPE ERROR: < 0.25 WAVE/cm @ 633nm.
SURFACE QUALITY: 20-10 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, LASER GRADE.
CRYSTALLOGRAPHIC ORIENTATION: a-PLANE +/- 15 ARC
MINUTES, WITH THE
c-AXIS 45 DEGREES TO
THE OD FLAT.
COATING: NONE, NOT REQUIRED.
SCD1481-01A
DIAMETER: 12.50mm + 0.00mm /- 0.10mmTHICKNESS: 3.00mm +/- 0.10mm
PARALLELISM: NOT SPECIFIED
EDGE BEVEL: PROTECTIVE EDGE BREAK, 2 PLACES.
TRANSMITTED WAVEFRONT ERROR: 1/10 WAVE MAXIMUM.
SURFACE FINISH: 40-20 PER MIL-O-13830, 2 FACES.
MATERIAL QUALITY: OPTICAL GRADE
CRYSTALLOGRAPHIC ORIENTATION: C AXIS PERPENDICULAR
TO THE FACES WITHIN 2 DEGREES.
MSW10M/010M
DIAMETER: 10.00mm +/- 0.05mmTHICKNESS: 1.00mm +/- 0.05mm
PARALLELISM: 5 ARC MINUTES MAXIMUM.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 60-40 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
SCD1906-01A
DIAMETER: 15.00mm + 0.00mm /- 0.05mmTHICKNESS: 6.35mm +/- 0.05mm
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
EDGE BEVEL: 0.10mm NOMINAL X 45deg, 2 PLACES.
SURFACE ACCURACY: NOT SPECIFIED.
SURFACE QUALITY: 40-20 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: C-AXIS PERPENDICULAR
TO THE SURFACE (0001) NOMINAL.
COATING: DUALBAND ANTIREFLECTIVE COATING FOR
0.50% MAXIMUM REFLECTANCE AT BOTH
1.064nm AND ALSO 800nm WITH A NORMAL
INCIDENCE ANGLE, APPLIED TO BOTH FACES.
A00IN0353046
DIAMETER: 0.3540"+/-.0010"THICKNESS: 0.0468"+/-.0010"
PARALLELISM: 5 ARC MINUTES MAXIMUM.
FLATNESS: 1/4 WAVE MAXIMUM, 2 FACES.
SURFACE FINISH: 20-10 PER MIL-O-13830, 2 FACES.
MATERIAL QUALITY: OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM
AK0910750040
DIAMETER TOLERANCE: +/-.002"THICKNESS TOLERANCE: +/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 1 POLISHED FACE.
SURFACE FINISH: 80-50 PER MIL-O-13830, 1 FACE.
16 MICROINCH NOMINAL, 1 FACE.
MATERIAL QUALITY: OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
SCD3405-02A
CONFIGURATION: DISC (WITH OD FLAT), PLANE-PARALLELDIAMETER: 0.620"+/-.001"
THICKNESS: 0.0100"+/-.0005"
PARALLELISM: CONTROLLED BY THICKNESS TOLERANCE.
EDGE BEVEL: NONE, NOT REQUIRED.
OD FLAT SIZE: 0.219" REF.ONLY (SEE DRAWING)
OD FLAT LOCATION: RANDOMLY LOCATED.
SURFACE FINISH: POLISHED BOTH FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: R-PLANE +/- 5 Deg.
COATING: NONE, NOT REQUIRED.