DIAMETER: 6.00mm + 0.00mm /- 0.10mm
THICKNESS: 1.60mm +/- 0.10mm
PARALLELISM: 2 ARC SECONDS MAXIMUM.
TRANSMITTED WAVEFRONT: 1/10 WAVE MAXIMUM AT 632nm.
EDGE BEVEL: 0.20mm +/- 0.10mm X 45deg, 2 PLACES.
SURFACE FINISH: 10-5 PER MIL-PRF-13830, 2 FACES.
CLEAR APERTURE: CENTRAL 4.5mm DIAMETER.
MATERIAL GRADE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: (0001) +/- 1/2deg.
COATING: NONE, NOT REQUIRED.
SCD2235-02A
$100.00
SAPPHIRE WINDOW 6.00mmDIA.
6.00mm DIA. X 1.60mm THK.
20 in stock
SKU: SCD2235-02A
Category: SAPPHIRE WINDOW
Weight | 0.1 lbs |
---|
Related products
MSW112/125A
DIAMETER: 1.125"+/-.004"THICKNESS: 0.125"+/-.003"
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
EDGE BEVEL: 0.010"/0.015" X 45deg, 2 PLACES.
SURFACE QUALITY: 80-50 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
SCD2191-02A
CONFIGURATION: DISC (W/ OD FLAT), PLANE-PARALLELDIAMETER: 2.000"+/-.002"
THICKNESS: 0.0157"+/-.0010"
OD FLAT SIZE: 0.625"+/-.050" WIDTH
OD FLAT LOCATION: RANDOM
PARALLELISM: 0.001" MAXIMUM T.I.R.
BOW: 0.0008" MAXIMUM T.I.R.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
SURFACE FINISH: 80-50 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
COATING: NONE, NOT REQUIRED.
SCD2006-02A
DIAMETER: 3.000"+/-.010" THICKNESS: 0.0380"+/-.0005" PARALLELISM: 30 SECONDS MAXIMUM OVER ANY 0.300"SQ. FLATNESS: POWER: 1.2 FRINGES MAXIMUM OVER ANY 0.300"SQ. IRREG: 0.6 FRINGES MAXIMUM OVER ANY 0.300"SQ. PRIMARY OD FLAT SIZE: 0.750"/1.000"WIDE PRIMARY OD FLAT LOCATION: 45deg +/- 1deg TO C-AXIS PROJECTION. SECONDARY OD FLAT SIZE: 0.380"/0.500"WIDE SECONDARY OD FLAT LOCATION: 90deg +/- 1deg TO PRIMARY FLAT EDGE. SURFACE FINISH: 40-20 OR BETTER ON SURFACE FACING UP WITH PRIMARY FLAT TO THE RIGNT AND SECONDARY FLAT TO THE TOP. BACK SURFACE 60-40 OR BETTER. MATERIAL TYPE: H.E.M.or CZ GROWN. CRYSTALLOGRHIC ORIENTATION: R-PLANE +/- 2deg.SCD1365-01B
DIAMETER: 20.00mm + 0.00mm /- 0.10mmTHICKNESS: 2.00mm +/- 0.10mm
PARALLELISM: 3 ARC MINUTES MAXIMUM.
EDGE BEVEL: SLIGHT PROTECTIVE BEVEL, 2 PLACES.
SURFACE FIGURE: 2.0 WAVES/INCH MAXIMUM, 2 FACES.
TRANSMITTED WAVEFRONT ERROR: 1/2 WAVE MAXIMUM.
SURFACE QUALITY: 60-40 SCRATCH/DIG PER
MIL-O-13830, TWO FACES
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: DUAL BAND ANTIREFLECTIVE COATED FOR
> 99.0% TRANSMISSION AT 2.94 MICRONS AND
85.0% MINIMUM TRANSMISSION AT 670nm, WITH
A 0-12deg INCIDENCE ANGLE, APPLIED TO
BOTH FACES. (RANDOM POLARIZATION)
DAMAGE THRESHOLD: 130 J/cm2, 10 Hz, 100usec PULSE
SCD1907-01A
DIAMETER: 22.00mm + 0.00mm /- 0.10mmTHICKNESS: 1.00mm +/- 0.10mm
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
EDGE BEVEL: 0.004" NOMINAL X 45deg, 2 PLACES.
SURFACE ACCURACY: NOT SPECIFIED.
SURFACE QUALITY: 10-5 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: ANTIREFLECTIVE HIGH DAMAGE THRESHOLD
COATING FOR MAXIMUM TRANSMISSION AT
0.635nm WITH A NORMAL INCIDENCE ANGLE,
APPLIED TO ONE FACE ONLY.
MSW250/125
CONFIGURATION: DISC, PLANE-PARALLELDIAMETER: 2.500"+/-.002"
THICKNESS: 0.125"+/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM
EDGE BEVEL: 0.010"/0.015" X 45deg, 2 PLACES.
SURFACE ACCURACY: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 80-50 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGAPHIC ORIENTATION: RANDOM
COATING: NONE, NOT REQUIRED.
A10910787019
DIAMETER: 20.00mm +/- 0.05mmTHICKNESS: 0.50mm +/- 0.05mm
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 OR BETTER, 1 FACE.
FINE GROUND OTHER FACE.
MATERIAL QUALITY: OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: C-AXIS PERPENDICULAR
TO FACES, (0001) NOMINAL.
SCD1481-01A
DIAMETER: 12.50mm + 0.00mm /- 0.10mmTHICKNESS: 3.00mm +/- 0.10mm
PARALLELISM: NOT SPECIFIED
EDGE BEVEL: PROTECTIVE EDGE BREAK, 2 PLACES.
TRANSMITTED WAVEFRONT ERROR: 1/10 WAVE MAXIMUM.
SURFACE FINISH: 40-20 PER MIL-O-13830, 2 FACES.
MATERIAL QUALITY: OPTICAL GRADE
CRYSTALLOGRAPHIC ORIENTATION: C AXIS PERPENDICULAR
TO THE FACES WITHIN 2 DEGREES.