LENGTH & WIDTH TOLERANCE: +/-.005″
THICKNESS: 0.0180″+/-.0002″
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 10-5 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: (0001) +/- 1 deg.
COATING: BROADBAND ANTIREFLECTIVE COATED FOR
< 0.25% REFLECTANCE FROM 1.30um TO
1.60um WITH A NORMAL INCIDENCE ANGLE,
APPLIED TO ONE FACE ONLY.
SCD2282-01A
$267.50
SAPPHIRE WINDOW RECT. COATED
0.760″ X 0.492″ X 0.018″THK.
1 in stock
SKU: SCD2282-01A
Category: SAPPHIRE WINDOW
Weight | 0.1 lbs |
---|
Related products
MSW25M/020M
DIAMETER: 25.00mm +/- 0.05mmTHICKNESS: 2.00mm +/- 0.05mm
PARALLELISM: 5 ARC MINUTES MAXIMUM.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 60-40 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
SCD1482-01A
DIAMETER: 0.750"+/-.010"THICKNESS: 0.039"+/-.004"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
EDGE BEVEL: NOT SPECIFIED.
SURFACE QUALITY: 60-40 SCRATCH-DIG PER MIL-O-13830
2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM
COATING: ITO HEATER, 5 WATTS/SQ" @ 12VAC OR VDC
AND Cr/Ni/Au BUSS BAR PER PRINT
APPROXIMATE RESISTANCE: 780 OHMS
MSW250/125
CONFIGURATION: DISC, PLANE-PARALLELDIAMETER: 2.500"+/-.002"
THICKNESS: 0.125"+/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM
EDGE BEVEL: 0.010"/0.015" X 45deg, 2 PLACES.
SURFACE ACCURACY: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 80-50 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGAPHIC ORIENTATION: RANDOM
COATING: NONE, NOT REQUIRED.
SCD1523-01A
DIAMETER: 0.500"+/-.002"THICKNESS: 0.125"+/-.002"
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES
EDGE BEVEL: 0.010"/0.015" X 45deg, 2 PLACES.
SURFACE FINISH: 80-50 PER MIL-O-13830, 2 FACES.
MATERIAL QUALITY: OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: ANTIREFLECTIVE COATED FOR MAXIMUM
TRANSMISSION AT 880 NANOMETERS WITH A
NORMAL INCIDENCE ANGLE, APPLIED TO 1 FACE
ONLY.
MARKING: ARROW ON OD SURFACE POINTING TOWARDS
COATED FACE.
SCD0651-01C
DIAMETER: 0.500"+.000"/-.001"THICKNESS: 0.0235"+/-.0005"
PARALELLISM: CONTROLLED BY THICKNESS TOLERANCE.
FLATNESS: 1 WAVE MAXIMUM, 2 FACES.
FINISH: 10 MICROINCH NOMINAL, 2 FACES.
OD EDGE: 0.012" FULL RADIUS
OD EDGE FINISH: BRUSH POLISH.
MATERIAL QUALITY: NON-OPTICAL
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
MSW112/125A
DIAMETER: 1.125"+/-.004"THICKNESS: 0.125"+/-.003"
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
EDGE BEVEL: 0.010"/0.015" X 45deg, 2 PLACES.
SURFACE QUALITY: 80-50 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
SCD3630-05B
CONFIGURATION: DISC, W/ OD FLAT, PLANE-PARALLELDIAMETER: 3.750"+.000"/-.005"
THICKNESS: 0.041"+/-.001"
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
PARALLELISM: 2 ARC SECONDS MAXIMUM
TRANSMITTED WAVEFRONT ERROR: < 1.0 WAVE @ 633nm.
RMS SLOPE ERROR: < 0.25 WAVE/cm @ 633nm.
SURFACE QUALITY: 20-10 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, LASER GRADE.
CRYSTALLOGRAPHIC ORIENTATION: a-PLANE +/- 15 ARC
MINUTES, WITH THE
c-AXIS 45 DEGREES TO
THE OD FLAT.
COATING: NONE, NOT REQUIRED.
AL0EW0393197
DIAMETER: 0.393"+/-.0020"THICKNESS: 0.197"+/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 5 WAVES MAXIMUM @ 0.633um, 2 FACES.
SURFACE FINISH: 20-10 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE
CRYSTALLOGRAPHIC ORIENTATION: (0001)