DIAMETER: 76.00mm +/- 0.10mm
THICKNESS: 3.00mm +/- 0.10mm
PARALLELISM: 5 ARC MINUTES MAXIMUM.
EDGE BEVEL: 0.20mm NOMINAL X 45deg, 2 PLACES
SURFACE ACCURACY: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 60-40 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: (0001) +/- 2deg
COATING: ANTIREFLECTIVE COAT FOR < 1.0%
REFLECTANCE PER SURFACE FROM 1300nm TO
1800nm WITH A NORMAL INCIDENCE ANGLE,
APPLIED TO BOTH FACES.
NOTE: COATING MUST BE ACID RESISTANT.
SCD2517-01C
$670.00
SAPPHIRE WINDOW 76mmD COATED
76.00mm DIA. X 3.00mm THK.
7 in stock
SKU: SCD2517-01C
Category: SAPPHIRE WINDOW
Weight | 0.1 lbs |
---|
Related products
SCD1871-WIT2
CONFIGURATION: DISC, PLANE-PARALLELDIAMETER: 1.000"+.000"/-.005"
THICKNESS: 2.50mm +/- 0.05mm
PARALLELISM: 0.03 DEGREES MAXIMUM.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
CLEAR APERTURE: CENTRAL 0.800" MINIMUM DIAMETER,
2 FACES.
SURFACE ACCURACY: PWR: 5 WAVES MAXIMUM, 2 FACES
IRRG: 2 WAVES MAXIMUM, 2 FACES
SURFACE QUALITY: 60-40 PER MIL-C-48497, 2 FACES.
SURFACE ROUGHNESS: 20 ANGSTROMS Ra MAXIMUM.
MATERIAL TYPE/QUALITY: SAPPHIRE, SCHLIEREN GRADE,
NO TWINNING, C-AXIS PERP.
TO FACES (NO BIREFRINGENCE)
COATING: NONE, UNCOATED SUBSTRATE.
SCD3630-05B
CONFIGURATION: DISC, W/ OD FLAT, PLANE-PARALLELDIAMETER: 3.750"+.000"/-.005"
THICKNESS: 0.041"+/-.001"
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
PARALLELISM: 2 ARC SECONDS MAXIMUM
TRANSMITTED WAVEFRONT ERROR: < 1.0 WAVE @ 633nm.
RMS SLOPE ERROR: < 0.25 WAVE/cm @ 633nm.
SURFACE QUALITY: 20-10 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, LASER GRADE.
CRYSTALLOGRAPHIC ORIENTATION: a-PLANE +/- 15 ARC
MINUTES, WITH THE
c-AXIS 45 DEGREES TO
THE OD FLAT.
COATING: NONE, NOT REQUIRED.
MSW25M/020M
DIAMETER: 25.00mm +/- 0.05mmTHICKNESS: 2.00mm +/- 0.05mm
PARALLELISM: 5 ARC MINUTES MAXIMUM.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 60-40 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
A00E10500157
DIAMETER TOLERANCE: +/-.002"THICKNESS TOLERANCE: +/-.004"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 OR BETTER, 2 FACES.
MATERIAL QUALITY: UNKNOWN.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
SCD0651-01C
DIAMETER: 0.500"+.000"/-.001"THICKNESS: 0.0235"+/-.0005"
PARALELLISM: CONTROLLED BY THICKNESS TOLERANCE.
FLATNESS: 1 WAVE MAXIMUM, 2 FACES.
FINISH: 10 MICROINCH NOMINAL, 2 FACES.
OD EDGE: 0.012" FULL RADIUS
OD EDGE FINISH: BRUSH POLISH.
MATERIAL QUALITY: NON-OPTICAL
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
SCD1523-01A
DIAMETER: 0.500"+/-.002"THICKNESS: 0.125"+/-.002"
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES
EDGE BEVEL: 0.010"/0.015" X 45deg, 2 PLACES.
SURFACE FINISH: 80-50 PER MIL-O-13830, 2 FACES.
MATERIAL QUALITY: OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: ANTIREFLECTIVE COATED FOR MAXIMUM
TRANSMISSION AT 880 NANOMETERS WITH A
NORMAL INCIDENCE ANGLE, APPLIED TO 1 FACE
ONLY.
MARKING: ARROW ON OD SURFACE POINTING TOWARDS
COATED FACE.
SCD1708-01A
DIAMETER: 0.116"+/-.001"THICKNESS: 0.038"+/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: BROADBAND ANTIREFLECTIVE WITH MgF2 FOR
MAXIMUM TRANSMISSION IN THE VISIBLE
ONE FACE ONLY.
MSW10M/010M
DIAMETER: 10.00mm +/- 0.05mmTHICKNESS: 1.00mm +/- 0.05mm
PARALLELISM: 5 ARC MINUTES MAXIMUM.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 60-40 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.