DIAMETER: 1.800″+/-.005″
THICKNESS: 0.125″+/-.005″
PARALLELISM: 20 ARC SECONDS MAXIMUM.
FLATNESS: 3 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 10-5 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE
CRYSTALLOGRAPHIC ORIENTATION: (0001)
SCD2538-02A
$350.00
SAPPHIRE WINDOW 1.800″DIA UC
1.800″DIA. X 0.125″THK.
SKU: SCD2538-02A
Category: SAPPHIRE WINDOW
Weight | 0.1 lbs |
---|
Related products
MSW25M/020M
DIAMETER: 25.00mm +/- 0.05mmTHICKNESS: 2.00mm +/- 0.05mm
PARALLELISM: 5 ARC MINUTES MAXIMUM.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 60-40 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
AL0EW0393197
DIAMETER: 0.393"+/-.0020"THICKNESS: 0.197"+/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 5 WAVES MAXIMUM @ 0.633um, 2 FACES.
SURFACE FINISH: 20-10 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE
CRYSTALLOGRAPHIC ORIENTATION: (0001)
SCD0651-01C
DIAMETER: 0.500"+.000"/-.001"THICKNESS: 0.0235"+/-.0005"
PARALELLISM: CONTROLLED BY THICKNESS TOLERANCE.
FLATNESS: 1 WAVE MAXIMUM, 2 FACES.
FINISH: 10 MICROINCH NOMINAL, 2 FACES.
OD EDGE: 0.012" FULL RADIUS
OD EDGE FINISH: BRUSH POLISH.
MATERIAL QUALITY: NON-OPTICAL
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
SCD2378-02B
CONFIGURATION: DISC (W/ OD FLATS), PLANE-PARALLELDIAMETER: 100.00mm +/- 0.10mm
THICKNESS: 0.025"+/-.0005"
PARALLELISM: 0.000138" T.T.V. ( 0.0035mm )
PRIMARY FLAT SIZE: 32.00mm +/- 2.00mm WIDTH
PRIMARY FLAT LOCATION: RANDOM.
SECONDARY FLAT SIZE: 18.00mm +/- 2.00mm WIDTH.
SECONDARY FLAT LOCATION: 90 deg FROM PRIMARY FLAT.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
SURFACE QUALITY: 80-50 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION:(0001)
AK0910750040
DIAMETER TOLERANCE: +/-.002"THICKNESS TOLERANCE: +/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 1 POLISHED FACE.
SURFACE FINISH: 80-50 PER MIL-O-13830, 1 FACE.
16 MICROINCH NOMINAL, 1 FACE.
MATERIAL QUALITY: OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
SCD3630-05B
CONFIGURATION: DISC, W/ OD FLAT, PLANE-PARALLELDIAMETER: 3.750"+.000"/-.005"
THICKNESS: 0.041"+/-.001"
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
PARALLELISM: 2 ARC SECONDS MAXIMUM
TRANSMITTED WAVEFRONT ERROR: < 1.0 WAVE @ 633nm.
RMS SLOPE ERROR: < 0.25 WAVE/cm @ 633nm.
SURFACE QUALITY: 20-10 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, LASER GRADE.
CRYSTALLOGRAPHIC ORIENTATION: a-PLANE +/- 15 ARC
MINUTES, WITH THE
c-AXIS 45 DEGREES TO
THE OD FLAT.
COATING: NONE, NOT REQUIRED.
SCD1767-02A
DIAMETER: 25.40mm + 0.000mm /- 0.127mmTHICKNESS: 0.61mm +/- 0.05mm
PARALLELISM: 1 ARC MINUTE MAXIMUM
FLATNESS: POWER: 2 FRINGES MAXIMUM WITHIN CLEAR
APERTURE, 2 FACES.
IRREG: 2 FRINGES MAXIMUM WITHIN CLEAR
APERTURE, 2 FACES.
CLEAR APERTURE: CENTRAL 21.5mm MINIMUM DIAMETER,
2 FACES.
SURFACE FINISH: E-E PER MIL-F-68497, WITHIN
CLEAR APERTURE, 2 FACES.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
EDGE CHIPS: PER MIL-O-13830.
MATERIAL TYPE/QUALITY: SAPPHIRE, PREMIUM GRADE.
CRYSTALLOGRAPHIC ORIENTATION: C-AXIS PERPENDICULAR
TO FACES WITHIN 2 DEGREES.
SCD1708-01A
DIAMETER: 0.116"+/-.001"THICKNESS: 0.038"+/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: BROADBAND ANTIREFLECTIVE WITH MgF2 FOR
MAXIMUM TRANSMISSION IN THE VISIBLE
ONE FACE ONLY.