MAJOR DIAMETER: 2.369″+/-.004″
MINOR DIAMETER: 1.982″+/-.004″
OVERALL THICKNESS: 0.300″+/-.002″
MINOR DIAMETER HEIGHT: 0.150″+/-.002″
PARALLELISM: 0.001″/INCH MAXIMUM T.I.R.
CONCENTRICITY: DIAMETERS WITHIN 0.002″.
EDGE RADII: 0.050″+/-.010″INSIDE AND OUTSIDE RADII
SURFACE ACCURACY: 6 FRINGES MAXIMUM WITH CLEAR
APERTURE, 2 FACES.
SURFACE QUALITY: 60-40 PER MIL-PRF-13830, 2 FACES.
LAND DIAMETER FACE: 1.732″+/-.004″ (TOP FACE)
MAJOR DIA. BEVELS: 0.020″+/-.005″ X 45deg, 2 PLCS.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: (0001).
COATING: NONE, NOT REQUIRED.
SCD2546-02A
$1,185.00
SAPPHIRE WINDOW 2.369″MAJ.DIA.
2.369″MAJOR DIA. X 0.300″THK.
2 in stock
SKU: SCD2546-02A
Category: SAPPHIRE WINDOW
Weight | 0.1 lbs |
---|
Related products
SCD1708-01A
DIAMETER: 0.116"+/-.001"THICKNESS: 0.038"+/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: BROADBAND ANTIREFLECTIVE WITH MgF2 FOR
MAXIMUM TRANSMISSION IN THE VISIBLE
ONE FACE ONLY.
A00E10500157
DIAMETER TOLERANCE: +/-.002"THICKNESS TOLERANCE: +/-.004"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 OR BETTER, 2 FACES.
MATERIAL QUALITY: UNKNOWN.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
SCD1907-01A
DIAMETER: 22.00mm + 0.00mm /- 0.10mmTHICKNESS: 1.00mm +/- 0.10mm
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
EDGE BEVEL: 0.004" NOMINAL X 45deg, 2 PLACES.
SURFACE ACCURACY: NOT SPECIFIED.
SURFACE QUALITY: 10-5 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: ANTIREFLECTIVE HIGH DAMAGE THRESHOLD
COATING FOR MAXIMUM TRANSMISSION AT
0.635nm WITH A NORMAL INCIDENCE ANGLE,
APPLIED TO ONE FACE ONLY.
MSW112/125A
DIAMETER: 1.125"+/-.004"THICKNESS: 0.125"+/-.003"
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
EDGE BEVEL: 0.010"/0.015" X 45deg, 2 PLACES.
SURFACE QUALITY: 80-50 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
SCD1365-01B
DIAMETER: 20.00mm + 0.00mm /- 0.10mmTHICKNESS: 2.00mm +/- 0.10mm
PARALLELISM: 3 ARC MINUTES MAXIMUM.
EDGE BEVEL: SLIGHT PROTECTIVE BEVEL, 2 PLACES.
SURFACE FIGURE: 2.0 WAVES/INCH MAXIMUM, 2 FACES.
TRANSMITTED WAVEFRONT ERROR: 1/2 WAVE MAXIMUM.
SURFACE QUALITY: 60-40 SCRATCH/DIG PER
MIL-O-13830, TWO FACES
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: DUAL BAND ANTIREFLECTIVE COATED FOR
> 99.0% TRANSMISSION AT 2.94 MICRONS AND
85.0% MINIMUM TRANSMISSION AT 670nm, WITH
A 0-12deg INCIDENCE ANGLE, APPLIED TO
BOTH FACES. (RANDOM POLARIZATION)
DAMAGE THRESHOLD: 130 J/cm2, 10 Hz, 100usec PULSE
SCD0651-01C
DIAMETER: 0.500"+.000"/-.001"THICKNESS: 0.0235"+/-.0005"
PARALELLISM: CONTROLLED BY THICKNESS TOLERANCE.
FLATNESS: 1 WAVE MAXIMUM, 2 FACES.
FINISH: 10 MICROINCH NOMINAL, 2 FACES.
OD EDGE: 0.012" FULL RADIUS
OD EDGE FINISH: BRUSH POLISH.
MATERIAL QUALITY: NON-OPTICAL
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
SCD2327-01A
DIAMETER: 0.560"+/-.002"THICKNESS: 0.040"+/-.002"
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
PERPENDICULARITY: 0.001"/INCH MAXIMUM T.I.R.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
EDGE BEVEL: 0.005"/0.010" X 45deg, 2 PLACES.
SURFACE FINISH: 80-50 OR BETTER PER MIL-PRF-13830,
2 FACES.
CLEAR APERATURE: 0.504" MINIMUM DIAMETER, BOTH
FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE
CRYSTALLOGRAPHIC ORIENTATION: RANDOM
COATING: ANTIREFLECTIVE COATED FOR MAXIMUM
TRANSMISSION IN THE VISIBLE SPECTRUM,
APPLIED TO BOTH FACES.
A10910787019
DIAMETER: 20.00mm +/- 0.05mmTHICKNESS: 0.50mm +/- 0.05mm
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 OR BETTER, 1 FACE.
FINE GROUND OTHER FACE.
MATERIAL QUALITY: OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: C-AXIS PERPENDICULAR
TO FACES, (0001) NOMINAL.