CONFIGURATION: DISC, PLANE-PARALLEL
DIAMETER: 1.575″+/-.005″
THICKNESS: 0.080″+/-.005″
PARALLELISM: 20 ARC SECONDS MAXIMUM.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
SURFACE ACCURACY: POWER: 1 WAVE MAXIMUM, 2 FACES
(@ 633nm) IRREG: 1/4 WAVE MAXIMUM,2 FACES
TRANSMITTED WAVEFRONT ERROR: 1/10 WAVE MAXIMUM
(@ 633nm) OVER CLEAR APERTURE.
SURFACE QUALITY: E-E PER MIL-F-48616 WITHIN CLEAR
APERTURE, 2 FACES.
CLEAR APERTURE: CENTRAL 0.750″ MINIMUM DIAMETER,
2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, CSI HEMEX GRADE
OR EQUIVALENT.
CRYSTALLOGRAPHIC ORIENTATION: (0001) +/- 2deg.
COATING: NONE, UNCOATED SUBSTRATE.
SCD2599-02A
$325.00
SAPPHIRE WINDOW COLD STOP UC
1.575″DIA. X 0.080″THK.
8 in stock
SKU: SCD2599-02A
Category: SAPPHIRE WINDOW
Weight | 0.1 lbs |
---|
Related products
SCD1907-01A
DIAMETER: 22.00mm + 0.00mm /- 0.10mmTHICKNESS: 1.00mm +/- 0.10mm
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
EDGE BEVEL: 0.004" NOMINAL X 45deg, 2 PLACES.
SURFACE ACCURACY: NOT SPECIFIED.
SURFACE QUALITY: 10-5 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: ANTIREFLECTIVE HIGH DAMAGE THRESHOLD
COATING FOR MAXIMUM TRANSMISSION AT
0.635nm WITH A NORMAL INCIDENCE ANGLE,
APPLIED TO ONE FACE ONLY.
SCD2378-02B
CONFIGURATION: DISC (W/ OD FLATS), PLANE-PARALLELDIAMETER: 100.00mm +/- 0.10mm
THICKNESS: 0.025"+/-.0005"
PARALLELISM: 0.000138" T.T.V. ( 0.0035mm )
PRIMARY FLAT SIZE: 32.00mm +/- 2.00mm WIDTH
PRIMARY FLAT LOCATION: RANDOM.
SECONDARY FLAT SIZE: 18.00mm +/- 2.00mm WIDTH.
SECONDARY FLAT LOCATION: 90 deg FROM PRIMARY FLAT.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
SURFACE QUALITY: 80-50 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION:(0001)
SCD2327-01A
DIAMETER: 0.560"+/-.002"THICKNESS: 0.040"+/-.002"
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
PERPENDICULARITY: 0.001"/INCH MAXIMUM T.I.R.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
EDGE BEVEL: 0.005"/0.010" X 45deg, 2 PLACES.
SURFACE FINISH: 80-50 OR BETTER PER MIL-PRF-13830,
2 FACES.
CLEAR APERATURE: 0.504" MINIMUM DIAMETER, BOTH
FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE
CRYSTALLOGRAPHIC ORIENTATION: RANDOM
COATING: ANTIREFLECTIVE COATED FOR MAXIMUM
TRANSMISSION IN THE VISIBLE SPECTRUM,
APPLIED TO BOTH FACES.
SCD3405-02A
CONFIGURATION: DISC (WITH OD FLAT), PLANE-PARALLELDIAMETER: 0.620"+/-.001"
THICKNESS: 0.0100"+/-.0005"
PARALLELISM: CONTROLLED BY THICKNESS TOLERANCE.
EDGE BEVEL: NONE, NOT REQUIRED.
OD FLAT SIZE: 0.219" REF.ONLY (SEE DRAWING)
OD FLAT LOCATION: RANDOMLY LOCATED.
SURFACE FINISH: POLISHED BOTH FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: R-PLANE +/- 5 Deg.
COATING: NONE, NOT REQUIRED.
A10910787019
DIAMETER: 20.00mm +/- 0.05mmTHICKNESS: 0.50mm +/- 0.05mm
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 OR BETTER, 1 FACE.
FINE GROUND OTHER FACE.
MATERIAL QUALITY: OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: C-AXIS PERPENDICULAR
TO FACES, (0001) NOMINAL.
SCD2006-02A
DIAMETER: 3.000"+/-.010" THICKNESS: 0.0380"+/-.0005" PARALLELISM: 30 SECONDS MAXIMUM OVER ANY 0.300"SQ. FLATNESS: POWER: 1.2 FRINGES MAXIMUM OVER ANY 0.300"SQ. IRREG: 0.6 FRINGES MAXIMUM OVER ANY 0.300"SQ. PRIMARY OD FLAT SIZE: 0.750"/1.000"WIDE PRIMARY OD FLAT LOCATION: 45deg +/- 1deg TO C-AXIS PROJECTION. SECONDARY OD FLAT SIZE: 0.380"/0.500"WIDE SECONDARY OD FLAT LOCATION: 90deg +/- 1deg TO PRIMARY FLAT EDGE. SURFACE FINISH: 40-20 OR BETTER ON SURFACE FACING UP WITH PRIMARY FLAT TO THE RIGNT AND SECONDARY FLAT TO THE TOP. BACK SURFACE 60-40 OR BETTER. MATERIAL TYPE: H.E.M.or CZ GROWN. CRYSTALLOGRHIC ORIENTATION: R-PLANE +/- 2deg.MSW112/125A
DIAMETER: 1.125"+/-.004"THICKNESS: 0.125"+/-.003"
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
EDGE BEVEL: 0.010"/0.015" X 45deg, 2 PLACES.
SURFACE QUALITY: 80-50 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
MSW10M/010M
DIAMETER: 10.00mm +/- 0.05mmTHICKNESS: 1.00mm +/- 0.05mm
PARALLELISM: 5 ARC MINUTES MAXIMUM.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 60-40 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.