CONFIGURATION: PLATE, PLANE-PARALLEL
LENGTH: 0.394″+/-.005″
WIDTH: 0.315″+/-.005″
THICKNESS: 0.039″+/-.005″
PARALLELISM: 10 ARC MINUTES MAXIMUM.
TRANSMITTED WAVEFRONT: 1/2 WAVE MAXIMUM @ 633nm.
SURFACE QUALITY: 40-20 PER MIL-PRF-13830, 2 FACES
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: (0001)
COATING: SURFACE “1”: PARTIAL REFLECTIVE COATED
FOR 1.00% +/- 0.30%
REFLECTANCE AT 2.94um WITH
A 45deg INCIDENCE ANGLE.
SURFACE “2”: ANTIREFLECTIVE COATED FOR
< 0.25% REFLECTANCE AT
2.94um WITH A 45deg
INCIDENCE ANGLE.
MARKING: ARROW ON EDGE SURFACE POINTING TOWARDS
SURFACE “1”.
SCD2606-01B
$100.00
SAPPHIRE WINDOW PICK-OFF 2.94
0.394″ X 0.315″ X 0.039″THK.
22 in stock
SKU: SCD2606-01B
Category: SAPPHIRE WINDOW
Weight | 0.1 lbs |
---|
Related products
SCD1906-01A
DIAMETER: 15.00mm + 0.00mm /- 0.05mmTHICKNESS: 6.35mm +/- 0.05mm
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
EDGE BEVEL: 0.10mm NOMINAL X 45deg, 2 PLACES.
SURFACE ACCURACY: NOT SPECIFIED.
SURFACE QUALITY: 40-20 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: C-AXIS PERPENDICULAR
TO THE SURFACE (0001) NOMINAL.
COATING: DUALBAND ANTIREFLECTIVE COATING FOR
0.50% MAXIMUM REFLECTANCE AT BOTH
1.064nm AND ALSO 800nm WITH A NORMAL
INCIDENCE ANGLE, APPLIED TO BOTH FACES.
AL0EW0393197
DIAMETER: 0.393"+/-.0020"THICKNESS: 0.197"+/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 5 WAVES MAXIMUM @ 0.633um, 2 FACES.
SURFACE FINISH: 20-10 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE
CRYSTALLOGRAPHIC ORIENTATION: (0001)
SCD1523-01A
DIAMETER: 0.500"+/-.002"THICKNESS: 0.125"+/-.002"
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES
EDGE BEVEL: 0.010"/0.015" X 45deg, 2 PLACES.
SURFACE FINISH: 80-50 PER MIL-O-13830, 2 FACES.
MATERIAL QUALITY: OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: ANTIREFLECTIVE COATED FOR MAXIMUM
TRANSMISSION AT 880 NANOMETERS WITH A
NORMAL INCIDENCE ANGLE, APPLIED TO 1 FACE
ONLY.
MARKING: ARROW ON OD SURFACE POINTING TOWARDS
COATED FACE.
AK0910750040
DIAMETER TOLERANCE: +/-.002"THICKNESS TOLERANCE: +/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 1 POLISHED FACE.
SURFACE FINISH: 80-50 PER MIL-O-13830, 1 FACE.
16 MICROINCH NOMINAL, 1 FACE.
MATERIAL QUALITY: OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
SCD1708-01A
DIAMETER: 0.116"+/-.001"THICKNESS: 0.038"+/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: BROADBAND ANTIREFLECTIVE WITH MgF2 FOR
MAXIMUM TRANSMISSION IN THE VISIBLE
ONE FACE ONLY.
SCD3630-05B
CONFIGURATION: DISC, W/ OD FLAT, PLANE-PARALLELDIAMETER: 3.750"+.000"/-.005"
THICKNESS: 0.041"+/-.001"
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
PARALLELISM: 2 ARC SECONDS MAXIMUM
TRANSMITTED WAVEFRONT ERROR: < 1.0 WAVE @ 633nm.
RMS SLOPE ERROR: < 0.25 WAVE/cm @ 633nm.
SURFACE QUALITY: 20-10 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, LASER GRADE.
CRYSTALLOGRAPHIC ORIENTATION: a-PLANE +/- 15 ARC
MINUTES, WITH THE
c-AXIS 45 DEGREES TO
THE OD FLAT.
COATING: NONE, NOT REQUIRED.
SCD1365-01B
DIAMETER: 20.00mm + 0.00mm /- 0.10mmTHICKNESS: 2.00mm +/- 0.10mm
PARALLELISM: 3 ARC MINUTES MAXIMUM.
EDGE BEVEL: SLIGHT PROTECTIVE BEVEL, 2 PLACES.
SURFACE FIGURE: 2.0 WAVES/INCH MAXIMUM, 2 FACES.
TRANSMITTED WAVEFRONT ERROR: 1/2 WAVE MAXIMUM.
SURFACE QUALITY: 60-40 SCRATCH/DIG PER
MIL-O-13830, TWO FACES
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: DUAL BAND ANTIREFLECTIVE COATED FOR
> 99.0% TRANSMISSION AT 2.94 MICRONS AND
85.0% MINIMUM TRANSMISSION AT 670nm, WITH
A 0-12deg INCIDENCE ANGLE, APPLIED TO
BOTH FACES. (RANDOM POLARIZATION)
DAMAGE THRESHOLD: 130 J/cm2, 10 Hz, 100usec PULSE
SCD1872-WIT
CONFIGURATION: DISC, PLANE-PARALLELDIAMETER: 1.000"+.000"/-.005"
THICKNESS: 2.50mm +/- 0.10mm
PARALLELISM: 0.03 DEGREES MAXIMUM.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
CLEAR APERTURE: CENTRAL 0.800" MINIMUM DIAMETER,
2 FACES.
SURFACE ACCURACY: PWR: 5 WAVES MAXIMUM, 2 FACES
IRRG: 2 WAVES MAXIMUM, 2 FACES
SURFACE QUALITY: 60-40 PER MIL-C-48497, 2 FACES.
SURFACE ROUGHNESS: 20 ANGSTROMS Ra MAXIMUM.
MATERIAL TYPE/QUALITY: SAPPHIRE, SCHLIEREN GRADE,
NO TWINNING, C-AXIS PERP.
TO FACES (NO BIREFRINGENCE)
COATING: NONE, UNCOATED SUBSTRATE.