DIAMETER: 0.250″+/-.005″
THICKNESS: 0.010″+/-.001″
PARALLELISM: CONTROLLED BY THICKNESS
FLATNESS: NOT SPECIFIED
EDGE BEVEL: POLISH EDGE ROLL, 2 PLACES.
SURFACE FINISH: 80-50 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, CSI OPTICAL GRADE
CRYSTALLOGRAPHIC ORIENTATION: (0001).
SCD2726-02A
$50.00
SAPPHIRE WINDOW 0.250″D 0.010″
0.250″DIA. X 0.010″THK.
12 in stock
SKU: SCD2726-02A
Category: SAPPHIRE WINDOW
Weight | 0.1 lbs |
---|
Related products
SCD1523-01A
DIAMETER: 0.500"+/-.002"THICKNESS: 0.125"+/-.002"
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES
EDGE BEVEL: 0.010"/0.015" X 45deg, 2 PLACES.
SURFACE FINISH: 80-50 PER MIL-O-13830, 2 FACES.
MATERIAL QUALITY: OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: ANTIREFLECTIVE COATED FOR MAXIMUM
TRANSMISSION AT 880 NANOMETERS WITH A
NORMAL INCIDENCE ANGLE, APPLIED TO 1 FACE
ONLY.
MARKING: ARROW ON OD SURFACE POINTING TOWARDS
COATED FACE.
A10910787019
DIAMETER: 20.00mm +/- 0.05mmTHICKNESS: 0.50mm +/- 0.05mm
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 OR BETTER, 1 FACE.
FINE GROUND OTHER FACE.
MATERIAL QUALITY: OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: C-AXIS PERPENDICULAR
TO FACES, (0001) NOMINAL.
SCD2378-02B
CONFIGURATION: DISC (W/ OD FLATS), PLANE-PARALLELDIAMETER: 100.00mm +/- 0.10mm
THICKNESS: 0.025"+/-.0005"
PARALLELISM: 0.000138" T.T.V. ( 0.0035mm )
PRIMARY FLAT SIZE: 32.00mm +/- 2.00mm WIDTH
PRIMARY FLAT LOCATION: RANDOM.
SECONDARY FLAT SIZE: 18.00mm +/- 2.00mm WIDTH.
SECONDARY FLAT LOCATION: 90 deg FROM PRIMARY FLAT.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
SURFACE QUALITY: 80-50 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION:(0001)
MSW112/125A
DIAMETER: 1.125"+/-.004"THICKNESS: 0.125"+/-.003"
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
EDGE BEVEL: 0.010"/0.015" X 45deg, 2 PLACES.
SURFACE QUALITY: 80-50 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
SCD1906-01A
DIAMETER: 15.00mm + 0.00mm /- 0.05mmTHICKNESS: 6.35mm +/- 0.05mm
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
EDGE BEVEL: 0.10mm NOMINAL X 45deg, 2 PLACES.
SURFACE ACCURACY: NOT SPECIFIED.
SURFACE QUALITY: 40-20 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: C-AXIS PERPENDICULAR
TO THE SURFACE (0001) NOMINAL.
COATING: DUALBAND ANTIREFLECTIVE COATING FOR
0.50% MAXIMUM REFLECTANCE AT BOTH
1.064nm AND ALSO 800nm WITH A NORMAL
INCIDENCE ANGLE, APPLIED TO BOTH FACES.
SCD2327-01A
DIAMETER: 0.560"+/-.002"THICKNESS: 0.040"+/-.002"
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
PERPENDICULARITY: 0.001"/INCH MAXIMUM T.I.R.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
EDGE BEVEL: 0.005"/0.010" X 45deg, 2 PLACES.
SURFACE FINISH: 80-50 OR BETTER PER MIL-PRF-13830,
2 FACES.
CLEAR APERATURE: 0.504" MINIMUM DIAMETER, BOTH
FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE
CRYSTALLOGRAPHIC ORIENTATION: RANDOM
COATING: ANTIREFLECTIVE COATED FOR MAXIMUM
TRANSMISSION IN THE VISIBLE SPECTRUM,
APPLIED TO BOTH FACES.
MSW250/125
CONFIGURATION: DISC, PLANE-PARALLELDIAMETER: 2.500"+/-.002"
THICKNESS: 0.125"+/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM
EDGE BEVEL: 0.010"/0.015" X 45deg, 2 PLACES.
SURFACE ACCURACY: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 80-50 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGAPHIC ORIENTATION: RANDOM
COATING: NONE, NOT REQUIRED.