DIAMETER: 0.500″+/-.001″
THICKNESS: 0.010″+/-.001″
PARALLELISM: 5 ARC MINUTES MAXIMUM.
FLATNESS: NOT SPECIFIED.
SURFACE FINISH: 80-50 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
SCD2809-02A
$25.00
SAPPHIRE WINDOW 0.500″DIA.
0.500″DIA. X 0.010″THK.
36 in stock
SKU: SCD2809-02A
Category: SAPPHIRE WINDOW
Weight | 0.1 lbs |
---|
Related products
SCD1481-01A
DIAMETER: 12.50mm + 0.00mm /- 0.10mmTHICKNESS: 3.00mm +/- 0.10mm
PARALLELISM: NOT SPECIFIED
EDGE BEVEL: PROTECTIVE EDGE BREAK, 2 PLACES.
TRANSMITTED WAVEFRONT ERROR: 1/10 WAVE MAXIMUM.
SURFACE FINISH: 40-20 PER MIL-O-13830, 2 FACES.
MATERIAL QUALITY: OPTICAL GRADE
CRYSTALLOGRAPHIC ORIENTATION: C AXIS PERPENDICULAR
TO THE FACES WITHIN 2 DEGREES.
A10910787019
DIAMETER: 20.00mm +/- 0.05mmTHICKNESS: 0.50mm +/- 0.05mm
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 OR BETTER, 1 FACE.
FINE GROUND OTHER FACE.
MATERIAL QUALITY: OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: C-AXIS PERPENDICULAR
TO FACES, (0001) NOMINAL.
A00IN0353046
DIAMETER: 0.3540"+/-.0010"THICKNESS: 0.0468"+/-.0010"
PARALLELISM: 5 ARC MINUTES MAXIMUM.
FLATNESS: 1/4 WAVE MAXIMUM, 2 FACES.
SURFACE FINISH: 20-10 PER MIL-O-13830, 2 FACES.
MATERIAL QUALITY: OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM
MSW112/125A
DIAMETER: 1.125"+/-.004"THICKNESS: 0.125"+/-.003"
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
EDGE BEVEL: 0.010"/0.015" X 45deg, 2 PLACES.
SURFACE QUALITY: 80-50 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
SCD1435-01A
MAJOR DIAMETER: 0.348"+/-.002"MINOR DIAMETER: 0.248"+.000"/-.005"
OVERALL THICKNESS: 0.097" REF.
MAJOR DIAMETER THICKNESS: 0.062"+/-.002"
MINOR DIAMETER HEIGHT: 0.035"+/-.005"
CONCENTRICITY OF DIAMETERS: NOT SPECIFIED.
PARALLELISM: 3 ARC MINUTES MAXIMUM
EDGE BEVEL: 0.005" NOMINAL X 45deg, 3 PLACES.
FLATNESS: 1 WAVE/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 60-40 PER MIL-O-13830, 2 FACES.
CLEAR APERTURE: CENTRAL 90% MINIMUM DIAMETER FACE
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL WHITE
GRADE (CSI).
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: NONE, NOT REQUIRED.
SCD1767-02A
DIAMETER: 25.40mm + 0.000mm /- 0.127mmTHICKNESS: 0.61mm +/- 0.05mm
PARALLELISM: 1 ARC MINUTE MAXIMUM
FLATNESS: POWER: 2 FRINGES MAXIMUM WITHIN CLEAR
APERTURE, 2 FACES.
IRREG: 2 FRINGES MAXIMUM WITHIN CLEAR
APERTURE, 2 FACES.
CLEAR APERTURE: CENTRAL 21.5mm MINIMUM DIAMETER,
2 FACES.
SURFACE FINISH: E-E PER MIL-F-68497, WITHIN
CLEAR APERTURE, 2 FACES.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
EDGE CHIPS: PER MIL-O-13830.
MATERIAL TYPE/QUALITY: SAPPHIRE, PREMIUM GRADE.
CRYSTALLOGRAPHIC ORIENTATION: C-AXIS PERPENDICULAR
TO FACES WITHIN 2 DEGREES.
SCD0651-01C
DIAMETER: 0.500"+.000"/-.001"THICKNESS: 0.0235"+/-.0005"
PARALELLISM: CONTROLLED BY THICKNESS TOLERANCE.
FLATNESS: 1 WAVE MAXIMUM, 2 FACES.
FINISH: 10 MICROINCH NOMINAL, 2 FACES.
OD EDGE: 0.012" FULL RADIUS
OD EDGE FINISH: BRUSH POLISH.
MATERIAL QUALITY: NON-OPTICAL
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
SCD3405-02A
CONFIGURATION: DISC (WITH OD FLAT), PLANE-PARALLELDIAMETER: 0.620"+/-.001"
THICKNESS: 0.0100"+/-.0005"
PARALLELISM: CONTROLLED BY THICKNESS TOLERANCE.
EDGE BEVEL: NONE, NOT REQUIRED.
OD FLAT SIZE: 0.219" REF.ONLY (SEE DRAWING)
OD FLAT LOCATION: RANDOMLY LOCATED.
SURFACE FINISH: POLISHED BOTH FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: R-PLANE +/- 5 Deg.
COATING: NONE, NOT REQUIRED.