DIAMETER: 60.00mm + 0.00mm /- 0.10mm
THICKNESS: 3.00mm +/- 0.10mm
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 7 WAVES MAXIMUM @ 633um, 2 FACES.
EDGE BEVEL: 0.50mm +/- 0.10mm X 45deg, 2 PLACES.
SURFACE FINISH: 80-50 PER MIL-PRF-13830, 2 FACES.
CLEAR APERTURE: CENTRAL 50mm MINIMUM DIAMETER.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: (0001) +/- 2deg.
COATING: NONE, NOT REQUIRED.
SCD2812-02A
$725.00
SAPPHIRE WINDOW 60.00mmDIA UC
60.00mm DIA. X 3.00mmTHK.
1 in stock
SKU: SCD2812-02A
Category: SAPPHIRE WINDOW
Weight | 0.1 lbs |
---|
Related products
SCD2006-02A
DIAMETER: 3.000"+/-.010" THICKNESS: 0.0380"+/-.0005" PARALLELISM: 30 SECONDS MAXIMUM OVER ANY 0.300"SQ. FLATNESS: POWER: 1.2 FRINGES MAXIMUM OVER ANY 0.300"SQ. IRREG: 0.6 FRINGES MAXIMUM OVER ANY 0.300"SQ. PRIMARY OD FLAT SIZE: 0.750"/1.000"WIDE PRIMARY OD FLAT LOCATION: 45deg +/- 1deg TO C-AXIS PROJECTION. SECONDARY OD FLAT SIZE: 0.380"/0.500"WIDE SECONDARY OD FLAT LOCATION: 90deg +/- 1deg TO PRIMARY FLAT EDGE. SURFACE FINISH: 40-20 OR BETTER ON SURFACE FACING UP WITH PRIMARY FLAT TO THE RIGNT AND SECONDARY FLAT TO THE TOP. BACK SURFACE 60-40 OR BETTER. MATERIAL TYPE: H.E.M.or CZ GROWN. CRYSTALLOGRHIC ORIENTATION: R-PLANE +/- 2deg.SCD1435-01A
MAJOR DIAMETER: 0.348"+/-.002"MINOR DIAMETER: 0.248"+.000"/-.005"
OVERALL THICKNESS: 0.097" REF.
MAJOR DIAMETER THICKNESS: 0.062"+/-.002"
MINOR DIAMETER HEIGHT: 0.035"+/-.005"
CONCENTRICITY OF DIAMETERS: NOT SPECIFIED.
PARALLELISM: 3 ARC MINUTES MAXIMUM
EDGE BEVEL: 0.005" NOMINAL X 45deg, 3 PLACES.
FLATNESS: 1 WAVE/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 60-40 PER MIL-O-13830, 2 FACES.
CLEAR APERTURE: CENTRAL 90% MINIMUM DIAMETER FACE
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL WHITE
GRADE (CSI).
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: NONE, NOT REQUIRED.
SCD2327-01A
DIAMETER: 0.560"+/-.002"THICKNESS: 0.040"+/-.002"
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
PERPENDICULARITY: 0.001"/INCH MAXIMUM T.I.R.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
EDGE BEVEL: 0.005"/0.010" X 45deg, 2 PLACES.
SURFACE FINISH: 80-50 OR BETTER PER MIL-PRF-13830,
2 FACES.
CLEAR APERATURE: 0.504" MINIMUM DIAMETER, BOTH
FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE
CRYSTALLOGRAPHIC ORIENTATION: RANDOM
COATING: ANTIREFLECTIVE COATED FOR MAXIMUM
TRANSMISSION IN THE VISIBLE SPECTRUM,
APPLIED TO BOTH FACES.
SCD1907-01A
DIAMETER: 22.00mm + 0.00mm /- 0.10mmTHICKNESS: 1.00mm +/- 0.10mm
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
EDGE BEVEL: 0.004" NOMINAL X 45deg, 2 PLACES.
SURFACE ACCURACY: NOT SPECIFIED.
SURFACE QUALITY: 10-5 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: ANTIREFLECTIVE HIGH DAMAGE THRESHOLD
COATING FOR MAXIMUM TRANSMISSION AT
0.635nm WITH A NORMAL INCIDENCE ANGLE,
APPLIED TO ONE FACE ONLY.
MSW25M/020M
DIAMETER: 25.00mm +/- 0.05mmTHICKNESS: 2.00mm +/- 0.05mm
PARALLELISM: 5 ARC MINUTES MAXIMUM.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 60-40 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
SCD1708-01A
DIAMETER: 0.116"+/-.001"THICKNESS: 0.038"+/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: BROADBAND ANTIREFLECTIVE WITH MgF2 FOR
MAXIMUM TRANSMISSION IN THE VISIBLE
ONE FACE ONLY.
SCD1481-01A
DIAMETER: 12.50mm + 0.00mm /- 0.10mmTHICKNESS: 3.00mm +/- 0.10mm
PARALLELISM: NOT SPECIFIED
EDGE BEVEL: PROTECTIVE EDGE BREAK, 2 PLACES.
TRANSMITTED WAVEFRONT ERROR: 1/10 WAVE MAXIMUM.
SURFACE FINISH: 40-20 PER MIL-O-13830, 2 FACES.
MATERIAL QUALITY: OPTICAL GRADE
CRYSTALLOGRAPHIC ORIENTATION: C AXIS PERPENDICULAR
TO THE FACES WITHIN 2 DEGREES.
SCD1767-02A
DIAMETER: 25.40mm + 0.000mm /- 0.127mmTHICKNESS: 0.61mm +/- 0.05mm
PARALLELISM: 1 ARC MINUTE MAXIMUM
FLATNESS: POWER: 2 FRINGES MAXIMUM WITHIN CLEAR
APERTURE, 2 FACES.
IRREG: 2 FRINGES MAXIMUM WITHIN CLEAR
APERTURE, 2 FACES.
CLEAR APERTURE: CENTRAL 21.5mm MINIMUM DIAMETER,
2 FACES.
SURFACE FINISH: E-E PER MIL-F-68497, WITHIN
CLEAR APERTURE, 2 FACES.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
EDGE CHIPS: PER MIL-O-13830.
MATERIAL TYPE/QUALITY: SAPPHIRE, PREMIUM GRADE.
CRYSTALLOGRAPHIC ORIENTATION: C-AXIS PERPENDICULAR
TO FACES WITHIN 2 DEGREES.