CONFIGURATION: DISC, TAPERED OD, PLANE-PARALLEL
MAJOR DIAMETER: 0.280″+/-.002″ (PRIOR TO BEVEL)
MINOR DIAMETER: 0.171″ REF.
THICKNESS: 0.150″+/-.005″
OD TAGER ANGLE: 20 DEGREES +/- 1/2 DEGREE
PARALLELISM: 1 ARC MINUTE MAXIMUM
FLATNESS: 1/4 WAVE MAXIMUM, 2 FACES.
SURFACE QUALITY: 60-40 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: (0001)
COATING: NONE, NOT REQUIRED.
SCD3163-02A
$225.00
SAPPHIRE WINDOW TAPERED OD
0.280″MAJOR DIA. X 0.150″THK.
4 in stock
SKU: SCD3163-02A
Category: SAPPHIRE WINDOW
Weight | 0.1 lbs |
---|
Related products
SCD1767-02A
DIAMETER: 25.40mm + 0.000mm /- 0.127mmTHICKNESS: 0.61mm +/- 0.05mm
PARALLELISM: 1 ARC MINUTE MAXIMUM
FLATNESS: POWER: 2 FRINGES MAXIMUM WITHIN CLEAR
APERTURE, 2 FACES.
IRREG: 2 FRINGES MAXIMUM WITHIN CLEAR
APERTURE, 2 FACES.
CLEAR APERTURE: CENTRAL 21.5mm MINIMUM DIAMETER,
2 FACES.
SURFACE FINISH: E-E PER MIL-F-68497, WITHIN
CLEAR APERTURE, 2 FACES.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
EDGE CHIPS: PER MIL-O-13830.
MATERIAL TYPE/QUALITY: SAPPHIRE, PREMIUM GRADE.
CRYSTALLOGRAPHIC ORIENTATION: C-AXIS PERPENDICULAR
TO FACES WITHIN 2 DEGREES.
MSW250/125
CONFIGURATION: DISC, PLANE-PARALLELDIAMETER: 2.500"+/-.002"
THICKNESS: 0.125"+/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM
EDGE BEVEL: 0.010"/0.015" X 45deg, 2 PLACES.
SURFACE ACCURACY: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 80-50 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGAPHIC ORIENTATION: RANDOM
COATING: NONE, NOT REQUIRED.
SCD1482-01A
DIAMETER: 0.750"+/-.010"THICKNESS: 0.039"+/-.004"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
EDGE BEVEL: NOT SPECIFIED.
SURFACE QUALITY: 60-40 SCRATCH-DIG PER MIL-O-13830
2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM
COATING: ITO HEATER, 5 WATTS/SQ" @ 12VAC OR VDC
AND Cr/Ni/Au BUSS BAR PER PRINT
APPROXIMATE RESISTANCE: 780 OHMS
MSW25M/020M
DIAMETER: 25.00mm +/- 0.05mmTHICKNESS: 2.00mm +/- 0.05mm
PARALLELISM: 5 ARC MINUTES MAXIMUM.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 60-40 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
MSW112/125A
DIAMETER: 1.125"+/-.004"THICKNESS: 0.125"+/-.003"
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
EDGE BEVEL: 0.010"/0.015" X 45deg, 2 PLACES.
SURFACE QUALITY: 80-50 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
SCD3630-05B
CONFIGURATION: DISC, W/ OD FLAT, PLANE-PARALLELDIAMETER: 3.750"+.000"/-.005"
THICKNESS: 0.041"+/-.001"
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
PARALLELISM: 2 ARC SECONDS MAXIMUM
TRANSMITTED WAVEFRONT ERROR: < 1.0 WAVE @ 633nm.
RMS SLOPE ERROR: < 0.25 WAVE/cm @ 633nm.
SURFACE QUALITY: 20-10 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, LASER GRADE.
CRYSTALLOGRAPHIC ORIENTATION: a-PLANE +/- 15 ARC
MINUTES, WITH THE
c-AXIS 45 DEGREES TO
THE OD FLAT.
COATING: NONE, NOT REQUIRED.
SCD3405-02A
CONFIGURATION: DISC (WITH OD FLAT), PLANE-PARALLELDIAMETER: 0.620"+/-.001"
THICKNESS: 0.0100"+/-.0005"
PARALLELISM: CONTROLLED BY THICKNESS TOLERANCE.
EDGE BEVEL: NONE, NOT REQUIRED.
OD FLAT SIZE: 0.219" REF.ONLY (SEE DRAWING)
OD FLAT LOCATION: RANDOMLY LOCATED.
SURFACE FINISH: POLISHED BOTH FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: R-PLANE +/- 5 Deg.
COATING: NONE, NOT REQUIRED.
SCD2378-02B
CONFIGURATION: DISC (W/ OD FLATS), PLANE-PARALLELDIAMETER: 100.00mm +/- 0.10mm
THICKNESS: 0.025"+/-.0005"
PARALLELISM: 0.000138" T.T.V. ( 0.0035mm )
PRIMARY FLAT SIZE: 32.00mm +/- 2.00mm WIDTH
PRIMARY FLAT LOCATION: RANDOM.
SECONDARY FLAT SIZE: 18.00mm +/- 2.00mm WIDTH.
SECONDARY FLAT LOCATION: 90 deg FROM PRIMARY FLAT.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
SURFACE QUALITY: 80-50 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION:(0001)