DIAMETER: 30.00mm + 0.00mm /- 0.25mm
THICKNESS: 5.00mm +/- 0.25mm
PARALLELISM: < 10 ARC MINUTES
FLATNESS: 1/4 WAVE MAXIMUM @ 633nm, 2 FACES.
EGGE BEVEL: 1.00mm +/- 0.10mm FACE WIDTH, 1 EDGE.
0.35mm MAXIMUM FACE WIDTH, OTHER EDGE
SURFACE FINISH: 60-40 PER MIL-PRF-13830, 2 FACES.
CLEAR APERTURE: CENTRAL 28.00mm MINIMUM DIAMETER.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: (0001)
COATING: ANTIREFLECTIVE COATED FOR < 0.50%
REFLECTANCE PER SURFACE AT 1550nm WITH
A NORMAL INCIDENCE ANGLE, APPLIED
TO BOTH FACES.
SCD3374-01B
$675.00
SAPPHIRE WINDOW LAMS COATED
30.00mm DIA. X 5.00mm THK.
1 in stock
Weight | 0.1 lbs |
---|
Related products
SCD1871-WIT2
CONFIGURATION: DISC, PLANE-PARALLELDIAMETER: 1.000"+.000"/-.005"
THICKNESS: 2.50mm +/- 0.05mm
PARALLELISM: 0.03 DEGREES MAXIMUM.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
CLEAR APERTURE: CENTRAL 0.800" MINIMUM DIAMETER,
2 FACES.
SURFACE ACCURACY: PWR: 5 WAVES MAXIMUM, 2 FACES
IRRG: 2 WAVES MAXIMUM, 2 FACES
SURFACE QUALITY: 60-40 PER MIL-C-48497, 2 FACES.
SURFACE ROUGHNESS: 20 ANGSTROMS Ra MAXIMUM.
MATERIAL TYPE/QUALITY: SAPPHIRE, SCHLIEREN GRADE,
NO TWINNING, C-AXIS PERP.
TO FACES (NO BIREFRINGENCE)
COATING: NONE, UNCOATED SUBSTRATE.
MSW10M/010M
DIAMETER: 10.00mm +/- 0.05mmTHICKNESS: 1.00mm +/- 0.05mm
PARALLELISM: 5 ARC MINUTES MAXIMUM.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 60-40 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
MSW250/125
CONFIGURATION: DISC, PLANE-PARALLELDIAMETER: 2.500"+/-.002"
THICKNESS: 0.125"+/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM
EDGE BEVEL: 0.010"/0.015" X 45deg, 2 PLACES.
SURFACE ACCURACY: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 80-50 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGAPHIC ORIENTATION: RANDOM
COATING: NONE, NOT REQUIRED.
A10910787019
DIAMETER: 20.00mm +/- 0.05mmTHICKNESS: 0.50mm +/- 0.05mm
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 OR BETTER, 1 FACE.
FINE GROUND OTHER FACE.
MATERIAL QUALITY: OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: C-AXIS PERPENDICULAR
TO FACES, (0001) NOMINAL.
SCD1708-01A
DIAMETER: 0.116"+/-.001"THICKNESS: 0.038"+/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: BROADBAND ANTIREFLECTIVE WITH MgF2 FOR
MAXIMUM TRANSMISSION IN THE VISIBLE
ONE FACE ONLY.
A00E10500157
DIAMETER TOLERANCE: +/-.002"THICKNESS TOLERANCE: +/-.004"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 OR BETTER, 2 FACES.
MATERIAL QUALITY: UNKNOWN.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
SCD1906-01A
DIAMETER: 15.00mm + 0.00mm /- 0.05mmTHICKNESS: 6.35mm +/- 0.05mm
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
EDGE BEVEL: 0.10mm NOMINAL X 45deg, 2 PLACES.
SURFACE ACCURACY: NOT SPECIFIED.
SURFACE QUALITY: 40-20 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: C-AXIS PERPENDICULAR
TO THE SURFACE (0001) NOMINAL.
COATING: DUALBAND ANTIREFLECTIVE COATING FOR
0.50% MAXIMUM REFLECTANCE AT BOTH
1.064nm AND ALSO 800nm WITH A NORMAL
INCIDENCE ANGLE, APPLIED TO BOTH FACES.
A00IN0353046
DIAMETER: 0.3540"+/-.0010"THICKNESS: 0.0468"+/-.0010"
PARALLELISM: 5 ARC MINUTES MAXIMUM.
FLATNESS: 1/4 WAVE MAXIMUM, 2 FACES.
SURFACE FINISH: 20-10 PER MIL-O-13830, 2 FACES.
MATERIAL QUALITY: OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM