DIAMETER: 10.00mm +/- 0.05mm
THICKNESS: 1.00mm +/- 0.05mm
PARALLELISM: 5 ARC MINUTES MAXIMUM
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES
SURFACE ACCURACY: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 60-40 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: ANTIRFLECTIVE COAT FOR MAXIMUM
TRANSMISSION FROM 400nm TO 700nm WITH
A NORMAL INCIDENCE ANGLE, APPLIED TO
BOTH FACES.
SCD3386-01A
$84.50
SAPPHIRE WINDOW 10.00mmDIA CTD
10.00mm DIA. X 1.00mm THK.
2 in stock
SKU: SCD3386-01A
Category: SAPPHIRE WINDOW
Weight | 0.1 lbs |
---|
Related products
SCD2191-02A
CONFIGURATION: DISC (W/ OD FLAT), PLANE-PARALLELDIAMETER: 2.000"+/-.002"
THICKNESS: 0.0157"+/-.0010"
OD FLAT SIZE: 0.625"+/-.050" WIDTH
OD FLAT LOCATION: RANDOM
PARALLELISM: 0.001" MAXIMUM T.I.R.
BOW: 0.0008" MAXIMUM T.I.R.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
SURFACE FINISH: 80-50 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
COATING: NONE, NOT REQUIRED.
SCD1523-01A
DIAMETER: 0.500"+/-.002"THICKNESS: 0.125"+/-.002"
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES
EDGE BEVEL: 0.010"/0.015" X 45deg, 2 PLACES.
SURFACE FINISH: 80-50 PER MIL-O-13830, 2 FACES.
MATERIAL QUALITY: OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: ANTIREFLECTIVE COATED FOR MAXIMUM
TRANSMISSION AT 880 NANOMETERS WITH A
NORMAL INCIDENCE ANGLE, APPLIED TO 1 FACE
ONLY.
MARKING: ARROW ON OD SURFACE POINTING TOWARDS
COATED FACE.
MSW10M/010M
DIAMETER: 10.00mm +/- 0.05mmTHICKNESS: 1.00mm +/- 0.05mm
PARALLELISM: 5 ARC MINUTES MAXIMUM.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 60-40 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
SCD1365-01B
DIAMETER: 20.00mm + 0.00mm /- 0.10mmTHICKNESS: 2.00mm +/- 0.10mm
PARALLELISM: 3 ARC MINUTES MAXIMUM.
EDGE BEVEL: SLIGHT PROTECTIVE BEVEL, 2 PLACES.
SURFACE FIGURE: 2.0 WAVES/INCH MAXIMUM, 2 FACES.
TRANSMITTED WAVEFRONT ERROR: 1/2 WAVE MAXIMUM.
SURFACE QUALITY: 60-40 SCRATCH/DIG PER
MIL-O-13830, TWO FACES
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: DUAL BAND ANTIREFLECTIVE COATED FOR
> 99.0% TRANSMISSION AT 2.94 MICRONS AND
85.0% MINIMUM TRANSMISSION AT 670nm, WITH
A 0-12deg INCIDENCE ANGLE, APPLIED TO
BOTH FACES. (RANDOM POLARIZATION)
DAMAGE THRESHOLD: 130 J/cm2, 10 Hz, 100usec PULSE
SCD1708-01A
DIAMETER: 0.116"+/-.001"THICKNESS: 0.038"+/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: BROADBAND ANTIREFLECTIVE WITH MgF2 FOR
MAXIMUM TRANSMISSION IN THE VISIBLE
ONE FACE ONLY.
SCD1481-01A
DIAMETER: 12.50mm + 0.00mm /- 0.10mmTHICKNESS: 3.00mm +/- 0.10mm
PARALLELISM: NOT SPECIFIED
EDGE BEVEL: PROTECTIVE EDGE BREAK, 2 PLACES.
TRANSMITTED WAVEFRONT ERROR: 1/10 WAVE MAXIMUM.
SURFACE FINISH: 40-20 PER MIL-O-13830, 2 FACES.
MATERIAL QUALITY: OPTICAL GRADE
CRYSTALLOGRAPHIC ORIENTATION: C AXIS PERPENDICULAR
TO THE FACES WITHIN 2 DEGREES.
A00E10500157
DIAMETER TOLERANCE: +/-.002"THICKNESS TOLERANCE: +/-.004"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 OR BETTER, 2 FACES.
MATERIAL QUALITY: UNKNOWN.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
AL0EW0393197
DIAMETER: 0.393"+/-.0020"THICKNESS: 0.197"+/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 5 WAVES MAXIMUM @ 0.633um, 2 FACES.
SURFACE FINISH: 20-10 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE
CRYSTALLOGRAPHIC ORIENTATION: (0001)