CONFIGURATION: DISC, PLANE-PARALLEL
DIAMETER: 1.000″+.000″/-.005″
THICKNESS: 2.50mm +/- 0.05mm
PARALLELISM: 0.03 DEGREES MAXIMUM.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
CLEAR APERTURE: CENTRAL 0.800″ MINIMUM DIAMETER,
2 FACES.
SURFACE ACCURACY: PWR: 5 WAVES MAXIMUM, 2 FACES
IRRG: 2 WAVES MAXIMUM, 2 FACES
SURFACE QUALITY: 60-40 PER MIL-C-48497, 2 FACES.
SURFACE ROUGHNESS: 20 ANGSTROMS Ra MAXIMUM.
MATERIAL TYPE/QUALITY: SAPPHIRE, SCHLIEREN GRADE,
NO TWINNING, C-AXIS PERP.
TO FACES (NO BIREFRINGENCE)
COATING: NONE, UNCOATED SUBSTRATE.
SCD1871-WIT2
$125.00
SAPPHIRE WINDOW 0.100″THK.
1.000″DIA. X 2.50mm THK.
4 in stock
SKU: SCD1871-WIT2
Category: SAPPHIRE WINDOW
Weight | 0.1 lbs |
---|
Related products
SCD1872-WIT
CONFIGURATION: DISC, PLANE-PARALLELDIAMETER: 1.000"+.000"/-.005"
THICKNESS: 2.50mm +/- 0.10mm
PARALLELISM: 0.03 DEGREES MAXIMUM.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
CLEAR APERTURE: CENTRAL 0.800" MINIMUM DIAMETER,
2 FACES.
SURFACE ACCURACY: PWR: 5 WAVES MAXIMUM, 2 FACES
IRRG: 2 WAVES MAXIMUM, 2 FACES
SURFACE QUALITY: 60-40 PER MIL-C-48497, 2 FACES.
SURFACE ROUGHNESS: 20 ANGSTROMS Ra MAXIMUM.
MATERIAL TYPE/QUALITY: SAPPHIRE, SCHLIEREN GRADE,
NO TWINNING, C-AXIS PERP.
TO FACES (NO BIREFRINGENCE)
COATING: NONE, UNCOATED SUBSTRATE.
A00E10500157
DIAMETER TOLERANCE: +/-.002"THICKNESS TOLERANCE: +/-.004"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 OR BETTER, 2 FACES.
MATERIAL QUALITY: UNKNOWN.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
SCD1907-01A
DIAMETER: 22.00mm + 0.00mm /- 0.10mmTHICKNESS: 1.00mm +/- 0.10mm
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
EDGE BEVEL: 0.004" NOMINAL X 45deg, 2 PLACES.
SURFACE ACCURACY: NOT SPECIFIED.
SURFACE QUALITY: 10-5 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: ANTIREFLECTIVE HIGH DAMAGE THRESHOLD
COATING FOR MAXIMUM TRANSMISSION AT
0.635nm WITH A NORMAL INCIDENCE ANGLE,
APPLIED TO ONE FACE ONLY.
SCD1481-01A
DIAMETER: 12.50mm + 0.00mm /- 0.10mmTHICKNESS: 3.00mm +/- 0.10mm
PARALLELISM: NOT SPECIFIED
EDGE BEVEL: PROTECTIVE EDGE BREAK, 2 PLACES.
TRANSMITTED WAVEFRONT ERROR: 1/10 WAVE MAXIMUM.
SURFACE FINISH: 40-20 PER MIL-O-13830, 2 FACES.
MATERIAL QUALITY: OPTICAL GRADE
CRYSTALLOGRAPHIC ORIENTATION: C AXIS PERPENDICULAR
TO THE FACES WITHIN 2 DEGREES.
A00IN0353046
DIAMETER: 0.3540"+/-.0010"THICKNESS: 0.0468"+/-.0010"
PARALLELISM: 5 ARC MINUTES MAXIMUM.
FLATNESS: 1/4 WAVE MAXIMUM, 2 FACES.
SURFACE FINISH: 20-10 PER MIL-O-13830, 2 FACES.
MATERIAL QUALITY: OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM
SCD2378-02A
CONFIGURATION: DISC (W/ OD FLATS), PLANE-PARALLELDIAMETER: 100.00mm +/- 0.10mm
THICKNESS: 0.025"+/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
PRIMARY FLAT SIZE: 32.00mm +/- 2.00mm WIDTH
PRIMARY FLAT LOCATION: RANDOM.
SECONDARY FLAT SIZE: 18.00mm +/- 2.00mm WIDTH.
SECONDARY FLAT LOCATION: 90 deg FROM PRIMARY FLAT.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
SURFACE QUALITY: 80-50 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALOGRAPHIC ORIENTATION: RANDOM
SCD1435-01A
MAJOR DIAMETER: 0.348"+/-.002"MINOR DIAMETER: 0.248"+.000"/-.005"
OVERALL THICKNESS: 0.097" REF.
MAJOR DIAMETER THICKNESS: 0.062"+/-.002"
MINOR DIAMETER HEIGHT: 0.035"+/-.005"
CONCENTRICITY OF DIAMETERS: NOT SPECIFIED.
PARALLELISM: 3 ARC MINUTES MAXIMUM
EDGE BEVEL: 0.005" NOMINAL X 45deg, 3 PLACES.
FLATNESS: 1 WAVE/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 60-40 PER MIL-O-13830, 2 FACES.
CLEAR APERTURE: CENTRAL 90% MINIMUM DIAMETER FACE
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL WHITE
GRADE (CSI).
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: NONE, NOT REQUIRED.
SCD2327-01A
DIAMETER: 0.560"+/-.002"THICKNESS: 0.040"+/-.002"
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
PERPENDICULARITY: 0.001"/INCH MAXIMUM T.I.R.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
EDGE BEVEL: 0.005"/0.010" X 45deg, 2 PLACES.
SURFACE FINISH: 80-50 OR BETTER PER MIL-PRF-13830,
2 FACES.
CLEAR APERATURE: 0.504" MINIMUM DIAMETER, BOTH
FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE
CRYSTALLOGRAPHIC ORIENTATION: RANDOM
COATING: ANTIREFLECTIVE COATED FOR MAXIMUM
TRANSMISSION IN THE VISIBLE SPECTRUM,
APPLIED TO BOTH FACES.