SCD1481-01A

SCD1872-WIT

CONFIGURATION: DISC, PLANE-PARALLEL
DIAMETER: 1.000"+.000"/-.005"
THICKNESS: 2.50mm +/- 0.10mm
PARALLELISM: 0.03 DEGREES MAXIMUM.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
CLEAR APERTURE: CENTRAL 0.800" MINIMUM DIAMETER,
2 FACES.
SURFACE ACCURACY: PWR: 5 WAVES MAXIMUM, 2 FACES
IRRG: 2 WAVES MAXIMUM, 2 FACES
SURFACE QUALITY: 60-40 PER MIL-C-48497, 2 FACES.
SURFACE ROUGHNESS: 20 ANGSTROMS Ra MAXIMUM.
MATERIAL TYPE/QUALITY: SAPPHIRE, SCHLIEREN GRADE,
NO TWINNING, C-AXIS PERP.
TO FACES (NO BIREFRINGENCE)
COATING: NONE, UNCOATED SUBSTRATE.

SCD2327-01A

DIAMETER: 0.560"+/-.002"
THICKNESS: 0.040"+/-.002"
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
PERPENDICULARITY: 0.001"/INCH MAXIMUM T.I.R.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
EDGE BEVEL: 0.005"/0.010" X 45deg, 2 PLACES.
SURFACE FINISH: 80-50 OR BETTER PER MIL-PRF-13830,
2 FACES.
CLEAR APERATURE: 0.504" MINIMUM DIAMETER, BOTH
FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE
CRYSTALLOGRAPHIC ORIENTATION: RANDOM
COATING: ANTIREFLECTIVE COATED FOR MAXIMUM
TRANSMISSION IN THE VISIBLE SPECTRUM,
APPLIED TO BOTH FACES.

SCD2378-02A

CONFIGURATION: DISC (W/ OD FLATS), PLANE-PARALLEL
DIAMETER: 100.00mm +/- 0.10mm
THICKNESS: 0.025"+/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
PRIMARY FLAT SIZE: 32.00mm +/- 2.00mm WIDTH
PRIMARY FLAT LOCATION: RANDOM.
SECONDARY FLAT SIZE: 18.00mm +/- 2.00mm WIDTH.
SECONDARY FLAT LOCATION: 90 deg FROM PRIMARY FLAT.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
SURFACE QUALITY: 80-50 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALOGRAPHIC ORIENTATION: RANDOM

SCD2006-02A

DIAMETER: 3.000"+/-.010" THICKNESS: 0.0380"+/-.0005" PARALLELISM: 30 SECONDS MAXIMUM OVER ANY 0.300"SQ. FLATNESS: POWER: 1.2 FRINGES MAXIMUM OVER ANY 0.300"SQ. IRREG: 0.6 FRINGES MAXIMUM OVER ANY 0.300"SQ. PRIMARY OD FLAT SIZE: 0.750"/1.000"WIDE PRIMARY OD FLAT LOCATION: 45deg +/- 1deg TO C-AXIS PROJECTION. SECONDARY OD FLAT SIZE: 0.380"/0.500"WIDE SECONDARY OD FLAT LOCATION: 90deg +/- 1deg TO PRIMARY FLAT EDGE. SURFACE FINISH: 40-20 OR BETTER ON SURFACE FACING UP WITH PRIMARY FLAT TO THE RIGNT AND SECONDARY FLAT TO THE TOP. BACK SURFACE 60-40 OR BETTER. MATERIAL TYPE: H.E.M.or CZ GROWN. CRYSTALLOGRHIC ORIENTATION: R-PLANE +/- 2deg.

MSW250/125

CONFIGURATION: DISC, PLANE-PARALLEL
DIAMETER: 2.500"+/-.002"
THICKNESS: 0.125"+/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM
EDGE BEVEL: 0.010"/0.015" X 45deg, 2 PLACES.
SURFACE ACCURACY: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 80-50 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGAPHIC ORIENTATION: RANDOM
COATING: NONE, NOT REQUIRED.

SCD1871-WIT2

CONFIGURATION: DISC, PLANE-PARALLEL
DIAMETER: 1.000"+.000"/-.005"
THICKNESS: 2.50mm +/- 0.05mm
PARALLELISM: 0.03 DEGREES MAXIMUM.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
CLEAR APERTURE: CENTRAL 0.800" MINIMUM DIAMETER,
2 FACES.
SURFACE ACCURACY: PWR: 5 WAVES MAXIMUM, 2 FACES
IRRG: 2 WAVES MAXIMUM, 2 FACES
SURFACE QUALITY: 60-40 PER MIL-C-48497, 2 FACES.
SURFACE ROUGHNESS: 20 ANGSTROMS Ra MAXIMUM.
MATERIAL TYPE/QUALITY: SAPPHIRE, SCHLIEREN GRADE,
NO TWINNING, C-AXIS PERP.
TO FACES (NO BIREFRINGENCE)
COATING: NONE, UNCOATED SUBSTRATE.

SCD1523-01A

DIAMETER: 0.500"+/-.002"
THICKNESS: 0.125"+/-.002"
PARALLELISM: 0.001"/INCH MAXIMUM T.I.R.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES
EDGE BEVEL: 0.010"/0.015" X 45deg, 2 PLACES.
SURFACE FINISH: 80-50 PER MIL-O-13830, 2 FACES.
MATERIAL QUALITY: OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: ANTIREFLECTIVE COATED FOR MAXIMUM
TRANSMISSION AT 880 NANOMETERS WITH A
NORMAL INCIDENCE ANGLE, APPLIED TO 1 FACE
ONLY.
MARKING: ARROW ON OD SURFACE POINTING TOWARDS
COATED FACE.

SCD0865-01A

DIAMETER TOLERANCE: +/-.002"
THICKNESS TOLERANCE: +/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE FINISH: 80-50 OR BETTER, 2 FACES.
MATERIAL QUALITY: OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM
COATING: ANTIREFLECTIVE COAT 1 FACE FOR MAXIMUM
TRANSMISSION AT 337nm. DOT ON OTHER SIDE