DIAMETER: 1.250″+/-.010″
THICKNESS: 0.040″+/-.001″
PARALLELISM: < 20 ARC SECONDS
EDGE BEVEL: 0.25mm MAXIMUM FACE WIDTH, 2 PLACES
TRANSMITTED WAVEFRONT: POWER: 1/4 WAVE MAXIMUM
(@ 633nm) IRREG: 1/10 WAVE MAXIMUM
SURFACE QUALITY: C-C PER MIL-C-48497A, 2 FACES.
SURFACE ROUGHNESS: < 25 ANGSTROMS RMS, 2 FACES.
CLEAR APERTURE: CENTRAL 0.680″ X 0.600″
RECTANGULAR AREA, BOTH FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, CSI HEMEX GRADE.
CRYSTALLOGRAPHIC ORIENTATION: (0001).
COATING: NONE, NOT REQUIRED.
SCD3382-02A
$235.00
SAPPHIRE WINDOW 1.250″DIA UC
1.250″DIA. X 0.040″THK.
19 in stock
SKU: SCD3382-02A
Category: SAPPHIRE WINDOW
Weight | 0.1 lbs |
---|
Related products
AL0EW0393197
DIAMETER: 0.393"+/-.0020"THICKNESS: 0.197"+/-.002"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 5 WAVES MAXIMUM @ 0.633um, 2 FACES.
SURFACE FINISH: 20-10 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE
CRYSTALLOGRAPHIC ORIENTATION: (0001)
SCD1482-01A
DIAMETER: 0.750"+/-.010"THICKNESS: 0.039"+/-.004"
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
EDGE BEVEL: NOT SPECIFIED.
SURFACE QUALITY: 60-40 SCRATCH-DIG PER MIL-O-13830
2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM
COATING: ITO HEATER, 5 WATTS/SQ" @ 12VAC OR VDC
AND Cr/Ni/Au BUSS BAR PER PRINT
APPROXIMATE RESISTANCE: 780 OHMS
MSW10M/010M
DIAMETER: 10.00mm +/- 0.05mmTHICKNESS: 1.00mm +/- 0.05mm
PARALLELISM: 5 ARC MINUTES MAXIMUM.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 60-40 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
SCD1871-WIT2
CONFIGURATION: DISC, PLANE-PARALLELDIAMETER: 1.000"+.000"/-.005"
THICKNESS: 2.50mm +/- 0.05mm
PARALLELISM: 0.03 DEGREES MAXIMUM.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
CLEAR APERTURE: CENTRAL 0.800" MINIMUM DIAMETER,
2 FACES.
SURFACE ACCURACY: PWR: 5 WAVES MAXIMUM, 2 FACES
IRRG: 2 WAVES MAXIMUM, 2 FACES
SURFACE QUALITY: 60-40 PER MIL-C-48497, 2 FACES.
SURFACE ROUGHNESS: 20 ANGSTROMS Ra MAXIMUM.
MATERIAL TYPE/QUALITY: SAPPHIRE, SCHLIEREN GRADE,
NO TWINNING, C-AXIS PERP.
TO FACES (NO BIREFRINGENCE)
COATING: NONE, UNCOATED SUBSTRATE.
MSW25M/020M
DIAMETER: 25.00mm +/- 0.05mmTHICKNESS: 2.00mm +/- 0.05mm
PARALLELISM: 5 ARC MINUTES MAXIMUM.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES
FLATNESS: 10 WAVES/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 60-40 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL GRADE.
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
SCD1435-01A
MAJOR DIAMETER: 0.348"+/-.002"MINOR DIAMETER: 0.248"+.000"/-.005"
OVERALL THICKNESS: 0.097" REF.
MAJOR DIAMETER THICKNESS: 0.062"+/-.002"
MINOR DIAMETER HEIGHT: 0.035"+/-.005"
CONCENTRICITY OF DIAMETERS: NOT SPECIFIED.
PARALLELISM: 3 ARC MINUTES MAXIMUM
EDGE BEVEL: 0.005" NOMINAL X 45deg, 3 PLACES.
FLATNESS: 1 WAVE/INCH MAXIMUM, 2 FACES.
SURFACE QUALITY: 60-40 PER MIL-O-13830, 2 FACES.
CLEAR APERTURE: CENTRAL 90% MINIMUM DIAMETER FACE
MATERIAL TYPE/QUALITY: SAPPHIRE, OPTICAL WHITE
GRADE (CSI).
CRYSTALLOGRAPHIC ORIENTATION: RANDOM.
COATING: NONE, NOT REQUIRED.
SCD3630-05B
CONFIGURATION: DISC, W/ OD FLAT, PLANE-PARALLELDIAMETER: 3.750"+.000"/-.005"
THICKNESS: 0.041"+/-.001"
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
PARALLELISM: 2 ARC SECONDS MAXIMUM
TRANSMITTED WAVEFRONT ERROR: < 1.0 WAVE @ 633nm.
RMS SLOPE ERROR: < 0.25 WAVE/cm @ 633nm.
SURFACE QUALITY: 20-10 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: SAPPHIRE, LASER GRADE.
CRYSTALLOGRAPHIC ORIENTATION: a-PLANE +/- 15 ARC
MINUTES, WITH THE
c-AXIS 45 DEGREES TO
THE OD FLAT.
COATING: NONE, NOT REQUIRED.
SCD1872-WIT
CONFIGURATION: DISC, PLANE-PARALLELDIAMETER: 1.000"+.000"/-.005"
THICKNESS: 2.50mm +/- 0.10mm
PARALLELISM: 0.03 DEGREES MAXIMUM.
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
CLEAR APERTURE: CENTRAL 0.800" MINIMUM DIAMETER,
2 FACES.
SURFACE ACCURACY: PWR: 5 WAVES MAXIMUM, 2 FACES
IRRG: 2 WAVES MAXIMUM, 2 FACES
SURFACE QUALITY: 60-40 PER MIL-C-48497, 2 FACES.
SURFACE ROUGHNESS: 20 ANGSTROMS Ra MAXIMUM.
MATERIAL TYPE/QUALITY: SAPPHIRE, SCHLIEREN GRADE,
NO TWINNING, C-AXIS PERP.
TO FACES (NO BIREFRINGENCE)
COATING: NONE, UNCOATED SUBSTRATE.