DIAMETER: 30.00mm + 0.00mm /- 0.10mm
THICKNESS: 0.750mm +/- 0.05mm
EDGE BEVELS: LIGHT PROTECTIVE BEVEL, 2 PLACES.
PARALLELISM: 3 ARC MINUTES MAXIMUM.
FLATNESS: 10 WAVES MAXIMUM AT 633nm, 2 FACES.
SURFACE QUALITY: 80-50 PER MIL-PRF-13830, 2 FACES.
CLEAR APERTURE: CENTRAL 25.50mm DIAMETER FACES.
MATERIAL TYPE/QUALITY: FUSED SILICA, STANDARD
OPTICAL GRADE.
COATING: NONE, NOT REQUIRED.
SCD3662-02A
$42.00
FUSED-SILICA WINDOW 30.00mmDIA
30.00mm DIA. X 0.750mm THK.
13 in stock
SKU: SCD3662-02A
Category: FUSED-SILICA WINDOW
Weight | 0.1 lbs |
---|
Related products
SCD2099-05A
DIAMETER: 1.500"+.000"/-.005"THICKNESS: 0.250"+/-.005"
PARALLELISM: 3 ARC MINUTES MAXIMUM
EDGE BEVEL: 0.010" NOMINAL X 45deg, 2 PLACES.
FLATNESS: 2 WAVES MAXIMUM AT 0.633um, 2 FACES.
SURFACE QUALITY: 60-40 PER MIL-O-13830, 2 FACES.
CLEAR APERTURE: CENTRAL 90% OF DIAMETER, 2 FACES.
MATERIAL TYPE/QUALITY: FUSED SILICA, INFRASIL 2,
WATER-FREE, OPTICAL GRADE.
COATING: NONE, NOT REQUIRED.
SCD2628-02A
CONFIGURATION: DISC, PLANE-PARALLELDIAMETER: 1.500"+.000"/-.005"
THICKNESS: 0.800"+/-.005"
PARALLELISM: 3 ARC MINUTES MAXIMUM
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
SURFACE ACCURACY: 1/4 WAVE MAXIMUM @633um, 2 FACES
SURFACE QUALITY: 60-40 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: FUSED SILICA, STANDARD
OPTICAL GRADE.
COATING: NONE, NOT REQUIRED.
SCD1695-01A
CONFIGURATION: DISC, TAPERED OD, PLANE-PARALLEL.MAJOR DIAMETER: 0.157" +.000/-.005
MINOR DIAMETER: 0.125 +/-.002"
OD TAPER ANGLE: 9.00deg REFERENCE
THICKNESS: 0.100" +.005/-.000"
PARALLELISM: 3 ARC MINUTES MAXIMUM
FLATNESS: 1 WAVE MAXIMUM, 2 FACES.
SURFACE FINISH: FACES: 80-50 PER MIL-O-13830.
MATERIAL TYPE/QUALITY: FUSED SILICA, SUPRASIL 1
SCD2559-02A
CONFIGURATION: PLATE, PLANE-PARALLELLENGTH: 1.180"+.000"/-.010"
WIDTH: 1.180"+.000"/-.010"
THICKNESS: 0.125"+/-.002"
CORNER BEVEL: 0.015" NOMINAL X 45deg, 2 PLACES.
EDGE BEVEL:: 0.010" NOMINAL X 45deg, 8 PLACES.
PARALLELISM: 3 ARC MINUTES MAXIMUM
SURFACE ACCURACY: NOT SPECIFIED.
SURFACE QUALITY: 80-50 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: FUSED SILICA, STANDARD
OPTICAL GRADE.
COATING: NONE, NOT REQUIRED.
SCD2099-02A
DIAMETER: 1.500"+.000"/-.005"THICKNESS: 0.250"+/-.005" (HIGH SIDE OF WEDGE)
WEDGE ANGLE: 3.0 DEGREES +/- 10 ARC MINUTES
EDGE BEVEL: 0.010" NOMINAL X 45deg, 2 PLACES.
FLATNESS: 2 WAVES MAXIMUM AT 0.633um, 2 FACES.
SURFACE QUALITY: 60-40 PER MIL-O-13830, 2 FACES.
CLEAR APERTURE: CENTRAL 90% OF DIAMETER, 2 FACES.
MATERIAL TYPE/QUALITY: FUSED SILICA, INFRASIL 2,
WATER-FREE, OPTICAL GRADE.
COATING: NONE, NOT REQUIRED.
SCD3667-01A
DIAMETER: 12.00mm + 0.00mm /- 0.10mmTHICKNESS: 0.125"+/-.0025" (HIGH SIDE OF WEDGE)
WEDGE ANGLE: 15 ARC MINUTES +/- 2 ARC MNIUTES
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
TRANSMITTED WAVEFRONT: 1/4 WAVE MAXIMUM @ 633nm
SURFACE QUALITY: 10-5 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: FUSED SILICA, STANDARD
OPTICAL GRADE.
COATING: ANTIREFLECTIVE COATED FOR MAXIMUM
TRANSMISSION FROM 630nm TO 900nm WITH
A NORMAL INCIDENCE ANGLE, APPLIED TO
BOTH FACES.
SCD3666-01A
DIAMETER: 6.00mm + 0.00mm /- 0.10mmTHICKNESS: 0.125"+/-.0025" (HIGH SIDE OF WEDGE)
WEDGE ANGLE: 15 ARC MINUTES +/- 2 ARC MNIUTES
EDGE BEVEL: LIGHT PROTECTIVE BEVEL, 2 PLACES.
TRANSMITTED WAVEFRONT: 1/4 WAVE MAXIMUM @ 633nm
SURFACE QUALITY: 10-5 PER MIL-PRF-13830, 2 FACES.
MATERIAL TYPE/QUALITY: FUSED SILICA, STANDARD
OPTICAL GRADE.
COATING: ANTIREFLECTIVE COATED FOR MAXIMUM
TRANSMISSION FROM 630nm TO 900nm WITH
A NORMAL INCIDENCE ANGLE, APPLIED TO
BOTH FACES.
SCD2046-02A
DIAMETER: 10.00mm + 0.00mm /- 0.10mmTHICKNESS: 1.00mm +/- 0.12mm
PARALLELISM: 10 ARC SECONDS MAXIMUM.
FLATNESS: 1/10 WAVE MAXIMUM, 2 FACES.
SURFACE FINISH: 10-5 PER MIL-O-13830, 2 FACES.
MATERIAL TYPE/QUALITY: FUSED SILICA, WATER-FREE,
INFRASIL 302.
COATING: NONE, NOT REQUIRED.